- 熔体流动速率 [g/10min]: 13.68
- 密度 [g/cm3]: 1.71
- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 223.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | Pigmentation can change mold shrinkage. | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | Pigmentation can change mold shrinkage. | ||
| Melt Flow | 13.68 g/10 min @Load 2.16 kg, Temperature 250 °C | 13.68 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | ISO 868 | ||
| Ball Indentation Hardness | 230 MPa | 33400 psi | H30; ISO 2039-1 | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | 5 mm/min; ISO 527-1/2 | ||
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527-1/2 | ||
| Tensile Modulus | 15.0 GPa | 2180 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| 6.50 J/cm² @Temperature -30.0 °C | 30.9 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.5 @Frequency 100 Hz | 4.5 @Frequency 100 Hz | IEC 60250 | ||
| 4.9 @Frequency 1e+6 Hz | 4.9 @Frequency 1e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.0040 @Frequency 100 Hz | 0.0040 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1e+6 Hz | 0.015 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 500 V | 500 V | Test Solution A, 100 drops; IEC 60112 | ||
| 525 V | 525 V | Test Solution A, CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 22.2 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 | ||
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 22.2 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 | ||
| Melting Point | 221 - 226 °C | 430 - 439 °F | DSC | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-1/2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/2 | ||
| Vicat Softening Point | 215 °C | 419 °F | 50N; ISO 306 | ||
| 220 °C | 428 °F | 10N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Oxygen Index | 20 % | 20 % | ISO 4589 | ||
| Glow Wire Test | 750 °C @Thickness 2.00 mm | 1380 °F @Thickness 0.0787 in | IEC 60695-2-1/0-3 | ||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 Step | IEC 60426 | |||