- 熔体流动速率 [g/10min]: 50.4
- 密度 [g/cm3]: 1.8
- 热变形温度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 2.00 mm | 0.0020 - 0.0040 in/in @Thickness 0.0787 in | sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.016 - 0.018 cm/cm | 0.016 - 0.018 in/in | |
| Melt Flow | 50.4 g/10 min @Load 2.16 kg, Temperature 250 °C | 50.4 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527-1/2 |
| Elongation at Break | 1.2 % | 1.2 % | ISO 527-1/2 |
| Tensile Modulus | 9.30 GPa | 1350 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 175 V | 175 V | Test Solution A CTI; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 310 °C | 590 °F | Short Term Heat Resistance after crosslinking (Soldering Tip) |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695 |
| V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | IEC 60695 | |