- 熔体流动速率 [g/10min]: 22.36
- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage | 0.002 cm/cm @Thickness 2.00 mm | 0.002 in/in @Thickness 0.0787 in | sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | |
| Melt Flow | 22.36 g/10 min @Load 2.16 kg, Temperature 250 °C | 22.36 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 230 MPa | 33400 psi | H30 (350 Kgy); ISO 2039-1 |
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/2 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527-1/2 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU |
| 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.850 J/cm² @Temperature -30.0 °C | 4.05 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 0.850 J/cm² @Temperature 23.0 °C | 4.05 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 11000 MPa | 1.60e+6 psi | Uncrosslinked; ISO 899-1 |
| 11000 MPa | 1.60e+6 psi | Crosslinked; ISO 899-1 | |
| Tensile Creep Modulus, 1000 hours | 7500 MPa | 1.09e+6 psi | Uncrosslinked; ISO 899-1 |
| 8500 MPa | 1.23e+6 psi | Crosslinked; ISO 899-1 | |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 |
| 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.0070 @Frequency 100 Hz | 0.0070 @Frequency 100 Hz | IEC 60250 |
| 0.018 @Frequency 1e+6 Hz | 0.018 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | Test Solution A CTI; IEC 60112 |
| 250 V | 250 V | 100 drops value; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1/-2 |
| Vicat Softening Point | 207 °C | 405 °F | Method B, 50 N; ISO 75-1/-2 |
| 215 °C | 419 °F | Method A, 10 N; ISO 75-1/-2 | |
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | IEC 60695 |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695 | |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695 | |