- 熔体流动速率 [g/10min]: 10.24
- 密度 [g/cm3]: 1.28
- 拉伸强度 [MPa]: 61.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.012 - 0.014 cm/cm @Thickness 2.00 mm | 0.012 - 0.014 in/in @Thickness 0.0787 in | sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | |
| Melt Flow | 10.24 g/10 min @Load 2.16 kg, Temperature 250 °C | 10.24 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 87 | 87 | ISO 868 |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | ISO 527-1/2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/2 |
| Elongation at Yield | 6.5 % | 6.5 % | ISO 527-1/2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 0.650 J/cm² @Temperature 23.0 °C | 3.09 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 44.4 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359, DIN 53752 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 44.4 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359, DIN 53752 |
| Vicat Softening Point | 150 °C | 302 °F | Method B, 50 N; ISO 306 |
| 210 °C | 410 °F | Method A, 10 N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695 |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695 | |