- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.1
- 拉伸强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | D792 |
| Water Absorption | 0.10 % | 0.10 % | 23°C•24h; D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa | 14500 psi | D638 |
| Elongation at Break | 4.0 % | 4.0 % | D638 |
| Flexural Strength | 170 MPa | 24700 psi | D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | D790 |
| Charpy Impact Unnotched | 4.20 J/cm² | 20.0 ft-lb/in² | IS0179 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | IS0179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | D257 |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | D149 |
| Dissipation Factor | 0.025 @Frequency 1e+6 Hz | 0.025 @Frequency 1e+6 Hz | D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 19.4 µin/in-°F @Temperature -22.0 - 86.0 °F | D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 255 - 265 °C | 491 - 509 °F | |
| Nozzle Temperature | 245 °C | 473 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Dry Time | 4 hour | 4 hour | 130°C-140°C |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | 3-15 sec |
| Back Pressure | 8.00 - 18.0 MPa | 1160 - 2610 psi | |