- 熔体流动速率 [g/10min]: 18.15
- 密度 [g/cm3]: 1.21
- 拉伸强度 [MPa]: 40.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | Pigmentation can change mold shrinkage. | ||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Pigmentation can change mold shrinkage. | ||
| Melt Flow | 18.15 g/10 min @Load 5.00 kg, Temperature 250 °C | 18.15 g/10 min @Load 11.0 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 65 | 65 | ISO 868 | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-1/2 | ||
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527-1/2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527-1/2 | ||
| Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | Partial Break; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | IEC 60250 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| Comparative Tracking Index | 575 V | 575 V | Test Solution A, 100 drops; IEC 60112 | ||
| >= 600 V | >= 600 V | Test Solution A, CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 150 µm/m-°C @Temperature 23.0 - 55.0 °C | 83.3 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 | ||
| CTE, linear, Transverse to Flow | 150 µm/m-°C @Temperature 23.0 - 55.0 °C | 83.3 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 | ||
| Melting Point | 221 - 226 °C | 430 - 439 °F | DSC | ||
| Vicat Softening Point | 125 °C | 257 °F | 50N; ISO 306 | ||
| 215 °C | 419 °F | 10N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 Step | IEC 60426 | |||