- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 0.05
- 弯曲模量 [MPa]: 5.50
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 175 MPa | 25400 psi | ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM D790 |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm | 584 kV/in @Thickness 0.0787 in | ASTM D149 |
| Dissipation Factor | 0.018 @Frequency 1e+6 Hz | 0.018 @Frequency 1e+6 Hz | ASTM D150 |
| Comparative Tracking Index | 600 V @Thickness 3.20 mm | 600 V @Thickness 0.126 in | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 55.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 30.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 225 - 255 °C | 437 - 491 °F | |
| Nozzle Temperature | 245 °C | 473 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
| Back Pressure | 8.00 - 18.0 MPa | 1160 - 2610 psi | |
| Screw Speed | <= 100 rpm | <= 100 rpm | |