Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT

Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT 物性表: Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT物性表及特性介绍,Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT注塑参数详情,如需Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT下载, 可到相关下载区下载
  • 吸水率 [%]: 0.07
  • 缺口冲击强度: 0.7
  • 弯曲模量 [MPa]: 5.60
  • 硬度: 120.0
  • 热变形温度 [℃]: 215.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.55 g/cc
@Temperature 23.0 °C
1.55 g/cc
@Temperature 73.4 °F
ASTM D792
Water Absorption 0.070 %
@Temperature 23.0 °C,
Time 86400 sec
0.070 %
@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0050 - 0.011 cm/cm
@Temperature 23.0 °C
0.0050 - 0.011 in/in
@Temperature 73.4 °F
ASTM D955
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 120120ASTM D785
Tensile Strength at Break 95.0 MPa13800 psi10mm/min; ASTM D638
Elongation at Break 3.4 %3.4 %10mm/min; ASTM D638
Flexural Strength 150 MPa21800 psi2mm/min; ASTM D790
Flexural Modulus 5.60 GPa812 ksi2mm/min; ASTM D790
Izod Impact, Notched 0.700 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C
1.31 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmASTM D257
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
@Thickness 6.40 mm
419 °F
@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
@Thickness 6.40 mm
401 °F
@Thickness 0.252 in
ASTM D648
Flammability, UL94  V-0
@Thickness 0.300 mm
V-0
@Thickness 0.0118 in
 V-0
@Thickness 0.750 mm
V-0
@Thickness 0.0295 in
 V-0
@Thickness 3.00 mm
V-0
@Thickness 0.118 in
 
Processing PropertiesMetricEnglishComments
Processing Temperature <= 265 °C<= 509 °F
Rear Barrel Temperature 220 - 240 °C428 - 464 °FStart Point: 235°C
Middle Barrel Temperature 235 - 255 °C455 - 491 °FStart Point: 245°C
Front Barrel Temperature 240 - 265 °C464 - 509 °FStart Point: 255°C
Melt Temperature 240 - 260 °C464 - 500 °FStart Point: 250°C
Mold Temperature 50.0 - 70.0 °C122 - 158 °FStart Point: 60°C
Drying Temperature 120 - 140 °C
@Time 14400 - 21600 sec
248 - 284 °F
@Time 4.00 - 6.00 hour
Pre-dry
 
Descriptive Properties
Glass Fiber Content (%)15
Injection SpeedModerate to High

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38623.html

免责声明: 本文 Kingfa PBT-RG151 Flame Retardant, 15% Glass Fiber Reinforced PBT 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4