- 熔体流动速率 [g/10min]: 60.8
- 密度 [g/cm3]: 1.52
- 弯曲模量 [MPa]: 10.0
- 热变形温度 [℃]: 224.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 |
| Melt Flow | 60.8 g/10 min @Load 5.00 kg, Temperature 260 °C | 60.8 g/10 min @Load 11.0 lb, Temperature 500 °F | ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-1,-2 |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 165 MPa | 23900 psi | 2 mm/min; ISO 178-A |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² @Temperature -30.0 °C | 15.7 ft-lb/in² @Temperature -22.0 °F | ISO 180-1U |
| 36.0 kJ/m² @Temperature 23.0 °C | 17.1 ft-lb/in² @Temperature 73.4 °F | ISO 180-1U | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | ISO 179-1eU |
| 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | ISO 179-1eU | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.30e+16 ohm-cm | 2.30e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 2.00e+16 ohm | 2.00e+16 ohm | IEC 60093 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | Solution A; UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 16.7 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 50.0 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| Melting Point | 220 °C | 428 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1,-2 |
| Vicat Softening Point | 206 °C | 403 °F | 50 N; 120 °C/h; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | |
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | 1.6 mm | |
| Oxygen Index | 43.7 % | 43.7 % | Method A; ISO 4589-2 |
| Glow Wire Test | 775 °C @Thickness 0.750 mm | 1430 °F @Thickness 0.0295 in | GWIT; IEC 60695-2-13 |
| 825 °C @Thickness 1.50 mm | 1520 °F @Thickness 0.0591 in | GWIT; IEC 60695-2-13 | |
| 850 °C @Thickness 0.400 mm | 1560 °F @Thickness 0.0157 in | GWIT; IEC 60695-2-13 | |
| 850 °C @Thickness 3.00 mm | 1560 °F @Thickness 0.118 in | GWIT; IEC 60695-2-13 | |
| 960 °C @Thickness 0.400 mm | 1760 °F @Thickness 0.0157 in | GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 0.750 mm | 1760 °F @Thickness 0.0295 in | GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | GWFI; IEC 60695-2-12 | |
| Shrinkage | 0.10 % | 0.10 % | post-shrinkage, 60x60x2; 120°C; 4 h; ISO 294-4 |
| 0.10 % | 0.10 % | post-shrinkage, transverse, 60x60x2; 120°C; 4 h; ISO 294-4 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 4.00 - 8.00 hour @Temperature 120 °C | 4.00 - 8.00 hour @Temperature 248 °F | |
| Moisture Content | 0.020 % | 0.020 % | Karl Fischer test |