- 缺口冲击强度: 0.35
- 弯曲模量 [MPa]: 3.825
- 硬度: 120.0
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 98.0 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 3.825 GPa | 554.8 ksi | ASTM D790 |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | ASTM D149 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |