Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber

Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber 物性表: Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber物性表及特性介绍,Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber注塑参数详情,如需Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 30.0
  • 缺口冲击强度: 10.0
  • 弯曲模量 [MPa]: 15.5
  • 热变形温度 [℃]: 225.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.69 g/cc1.69 g/ccISO 1183
Bulk Density 0.800 g/cc0.0289 lb/in³ISO 60
Linear Mold Shrinkage, Flow 0.0020 cm/cm0.0020 in/in60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
 0.0080 cm/cm0.0080 in/inPost-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm0.0010 in/inPost-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
 0.0080 cm/cm0.0080 in/in60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4
Melt Flow 30 g/10 min
@Load 5.00 kg,
Temperature 260 °C
30 g/10 min
@Load 11.0 lb,
Temperature 500 °F
ISO 1133-1
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 160 MPa23200 psiISO 527-1, -2; 5 mm/min
Elongation at Break 1.9 %1.9 %ISO 527-1, -2; 5 mm/min
Tensile Modulus 16.0 GPa2320 ksiISO 527-1, -2; 1 mm/min
Flexural Strength 260 MPa
@Strain 2.10 %
37700 psi
@Strain 2.10 %
2 mm/min; ISO 178-A
Flexural Modulus 15.5 GPa2250 ksi2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)  <= 10.0 kJ/m²
@Temperature 23.0 °C
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 180-1A
 <= 10.0 kJ/m²
@Temperature -30.0 °C
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 180-1A
Izod Impact, Unnotched (ISO)  55.0 kJ/m²
@Temperature 23.0 °C
26.2 ft-lb/in²
@Temperature 73.4 °F
ISO 180-1U
 60.0 kJ/m²
@Temperature -30.0 °C
28.6 ft-lb/in²
@Temperature -22.0 °F
ISO 180-1U
Charpy Impact Unnotched  6.00 J/cm²
@Temperature 23.0 °C
28.6 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eU
 6.50 J/cm²
@Temperature -30.0 °C
30.9 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eU
Charpy Impact, Notched  <= 1.00 J/cm²
@Temperature 23.0 °C
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eA
 <= 1.00 J/cm²
@Temperature -30.0 °C
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index 250 V250 Vd.a.m.; Solution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
11.1 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1, -2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
44.4 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1, -2
Melting Point 225 - 250 °C437 - 482 °F10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 225 °C437 °FISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C401 °FISO 75-1, -2
Vicat Softening Point 210 °C
@Load 5.10 kg
410 °F
@Load 11.2 lb
120°C/hour; ISO 306
 
Processing PropertiesMetricEnglishComments
Melt Temperature 260 - 280 °C500 - 536 °F
 270 °C518 °Ffor test specimens; ISO 294
Mold Temperature 80.0 - 100 °C176 - 212 °F
 90.0 °C194 °Ffor test specimens; ISO 294
Drying Temperature 120 °C248 °F
Dry Time 4 - 8 hour4 - 8 hour
Moisture Content 0.00 - 0.020 %0.00 - 0.020 %residual; Karl Fischer Test
 
Descriptive Properties
ISO ShortnameISO 7792-1-PBT+PET, GHMR, 09-160, GF45

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38681.html

免责声明: 本文 Lanxess Pocan® ECO T 3240 000000 PBT + PET, 45% Glass Fiber 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4