Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber

Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber 物性表: Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber物性表及特性介绍,Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber注塑参数详情,如需Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 24.0
  • 缺口冲击强度: 10.0
  • 断裂伸长率 [%]: 160
  • 弯曲模量 [MPa]: 5.60
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.40 g/cc1.40 g/ccISO 1183
Bulk Density 0.700 g/cc0.0253 lb/in³ISO 60
Linear Mold Shrinkage, Flow 0.0010 cm/cm0.0010 in/inPost-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
 0.0060 cm/cm0.0060 in/in60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm0.0010 in/inPost-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
 0.010 cm/cm0.010 in/in60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Melt Flow 24 g/10 min
@Load 2.16 kg,
Temperature 260 °C
24 g/10 min
@Load 4.76 lb,
Temperature 500 °F
ISO 1133-1
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 100 MPa14500 psiISO 527-1, -2; 5 mm/min
Elongation at Break 3.7 %3.7 %ISO 527-1, -2; 5 mm/min
Tensile Modulus 5.90 GPa856 ksiISO 527-1, -2; 1 mm/min
Flexural Strength 165 MPa
@Strain 4.40 %
23900 psi
@Strain 4.40 %
2 mm/min; ISO 178-A
Flexural Yield Strength 160 MPa
@Strain 3.50 %
23200 psi
@Strain 3.50 %
2 mm/min; ISO 178-A
Flexural Modulus 5.60 GPa812 ksi2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)  <= 10.0 kJ/m²
@Temperature 23.0 °C
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 180-1A
 <= 10.0 kJ/m²
@Temperature -30.0 °C
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 180-1A
Izod Impact, Unnotched (ISO)  30.0 kJ/m²
@Temperature -30.0 °C
14.3 ft-lb/in²
@Temperature -22.0 °F
ISO 180-1U
 45.0 kJ/m²
@Temperature 23.0 °C
21.4 ft-lb/in²
@Temperature 73.4 °F
ISO 180-1U
Charpy Impact Unnotched  3.50 J/cm²
@Temperature -30.0 °C
16.7 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eU
 5.00 J/cm²
@Temperature 23.0 °C
23.8 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eU
Charpy Impact, Notched  <= 1.00 J/cm²
@Temperature 23.0 °C
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1eA
 <= 1.00 J/cm²
@Temperature -30.0 °C
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 179-1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
Dielectric Strength 36.0 kV/mm
@Thickness 1.00 mm
914 kV/in
@Thickness 0.0394 in
IEC 60243-1
Comparative Tracking Index 275 V275 Vd.a.m.; Solution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
22.2 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1, -2
CTE, linear, Transverse to Flow 130 µm/m-°C
@Temperature 23.0 - 55.0 °C
72.2 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1, -2
Melting Point 225 °C437 °F10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C374 °FISO 75-1, -2
Vicat Softening Point 200 °C
@Load 5.10 kg
392 °F
@Load 11.2 lb
120°C/hour; ISO 306
Flammability, UL94  HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
 HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
 
Processing PropertiesMetricEnglishComments
Melt Temperature 250 - 270 °C482 - 518 °F
 260 °C500 °Ffor test specimens; ISO 294
Mold Temperature 80.0 °C176 °Ffor test specimens; ISO 294
 80.0 - 100 °C176 - 212 °F
Drying Temperature 120 °C248 °F
Dry Time 4 - 8 hour4 - 8 hour
Moisture Content 0.00 - 0.020 %0.00 - 0.020 %residual; Karl Fischer Test
 
Descriptive Properties
ISO ShortnameISO 7792-1-PBT, GHMR, 09-050, GF16

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38682.html

免责声明: 本文 Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4