- 熔体流动速率 [g/10min]: 53.0
- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.35
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.35 % | 0.35 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 53 g/10 min @Load 5.00 kg, Temperature 260 °C | 53 g/10 min @Load 11.0 lb, Temperature 500 °F | Calculated from MVR using melt density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.2 % | 2.2 % | ISO 527-1/-2 | ||
| 3.0 % | 3.0 % | Nominal; ISO 527-1/-2 | |||
| Tensile Modulus | 10.6 GPa | 1540 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Impact | 669 | 669 | Puncture maximum force (N); ISO 6603-2 | ||
| 649 @Temperature -30.0 °C | 649 @Temperature -22.0 °F | Puncture maximum force (N); ISO 6603-2 | |||
| Puncture Energy | 2.30 J | 1.70 ft-lb | ISO 6603-2 | ||
| 2.10 J @Temperature -30.0 °C | 1.55 ft-lb @Temperature -22.0 °F | ISO 6603-2 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.9 @Frequency 100 Hz | 3.9 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0060 @Frequency 100 Hz | 0.0060 @Frequency 100 Hz | IEC 60250 | ||
| 0.052 @Frequency 1.00e+6 Hz | 0.052 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 275 V | 275 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 135 °C | 275 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 | ||
| Oxygen Index | 32 % | 32 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Additives | Flame retarding agent | ||||
| Release agent | |||||
| Features | Flame retardant | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT,GFHMR,09-110,GF30; ISO 1043-PBT GF FR(17) | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||