- 熔体流动速率 [g/10min]: 236.0
- 密度 [g/cm3]: 1.31
- 拉伸强度 [MPa]: 56.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 236 g/10 min @Load 2.16 kg, Temperature 250 °C | 236 g/10 min @Load 4.76 lb, Temperature 482 °F | Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.9 % | 2.9 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 2.9 % | 2.9 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1/-2 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT,G,05-030 | ||||
| Processing | Blow molding | ||||
| Injection molding | |||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.