- 熔体流动速率 [g/10min]: 23.0
- 密度 [g/cm3]: 1.66
- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm | 0.0028 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0091 cm/cm | 0.0091 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 260 °C | 23 g/10 min @Load 4.76 lb, Temperature 500 °F | Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-1/-2 | ||
| Tensile Modulus | 10.6 GPa | 1540 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Impact | 780 | 780 | Puncture maximum force (N); ISO 6603-2 | ||
| 720 @Temperature -30.0 °C | 720 @Temperature -22.0 °F | Puncture maximum force (N); ISO 6603-2 | |||
| Puncture Energy | 1.90 J | 1.40 ft-lb | ISO 6603-2 | ||
| 1.70 J @Temperature -30.0 °C | 1.25 ft-lb @Temperature -22.0 °F | ISO 6603-2 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.1 @Frequency 100 Hz | 4.1 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0030 @Frequency 100 Hz | 0.0030 @Frequency 100 Hz | IEC 60250 | ||
| 0.0165 @Frequency 1.00e+6 Hz | 0.0165 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 227 °C | 441 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 137 °C | 279 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| Oxygen Index | 32 % | 32 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Features | Flame retardant | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-PBT,GFHMR,09-110,GF30; ISO 1043-PBT GF FR(17) | ||||
| Processing | Injection molding | ||||