- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 0.13
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 28.3
- 断裂伸长率 [%]: 39.2
- 弯曲强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.24
- 硬度: 105.0
- 热变形温度 [℃]: 60.0
- 透光率 [%]: 82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 - 1.33 g/cc | 0.0426 - 0.0480 lb/in³ | Average value: 1.27 g/cc Grade Count:20 |
| Water Absorption | 0.130 - 0.200 % | 0.130 - 0.200 % | Average value: 0.153 % Grade Count:3 |
| Linear Mold Shrinkage | 0.00200 - 0.00600 cm/cm | 0.00200 - 0.00600 in/in | Average value: 0.00400 cm/cm Grade Count:11 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 - 119 | 105 - 119 | Average value: 110 Grade Count:7 |
| Tensile Strength, Ultimate | 26.0 - 57.9 MPa | 3770 - 8400 psi | Average value: 39.5 MPa Grade Count:17 |
| Tensile Strength, Yield | 28.3 - 58.6 MPa | 4100 - 8500 psi | Average value: 48.0 MPa Grade Count:10 |
| Elongation at Break | 5.00 - 350 % | 5.00 - 350 % | Average value: 104 % Grade Count:17 |
| Elongation at Yield | 3.90 - 4.10 % | 3.90 - 4.10 % | Average value: 4.00 % Grade Count:5 |
| Modulus of Elasticity | 1.10 - 2.69 GPa | 160 - 390 ksi | Average value: 1.93 GPa Grade Count:16 |
| Flexural Yield Strength | 39.2 - 88.9 MPa | 5690 - 12900 psi | Average value: 72.0 MPa Grade Count:16 |
| Flexural Modulus | 1.24 - 2.76 GPa | 180 - 400 ksi | Average value: 1.99 GPa Grade Count:18 |
| Izod Impact, Notched | 0.267 - 10.7 J/cm | 0.500 - 20.0 ft-lb/in | Average value: 3.01 J/cm Grade Count:13 |
| 0.270 - 0.520 J/cm @Temperature -40.0 - -40.0 °C | 0.506 - 0.974 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.360 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 0.497 - 13.3 J/cm | 0.930 - 25.0 ft-lb/in | Average value: 6.94 J/cm Grade Count:7 |
| 0.277628 - 0.277628 J/cm @Temperature -40.0 - -40.0 °C | 0.520111 - 0.520111 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.278 J/cm Grade Count:1 | |
| Charpy Impact Unnotched | NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:2 |
| Charpy Impact, Notched | 0.310 - 0.370 J/cm² @Temperature -30.0 - -30.0 °C | 1.48 - 1.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 0.340 J/cm² Grade Count:2 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+15 ohm-cm | 10.0 - 1.00e+15 ohm-cm | Average value: 1.67e+14 ohm-cm Grade Count:12 |
| Surface Resistance | 1000 - 1.00e+16 ohm | 1000 - 1.00e+16 ohm | Average value: 6.67e+14 ohm Grade Count:9 |
| Static Decay | 0.0100 - 2.00 sec | 0.0100 - 2.00 sec | Average value: 1.03 sec Grade Count:7 |
| Dielectric Constant | 2.40 - 2.60 | 2.40 - 2.60 | Average value: 2.50 Grade Count:3 |
| Dielectric Strength | 16.0 - 16.1 kV/mm | 406 - 410 kV/in | Average value: 16.1 kV/mm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 43.0 - 100 µm/m-°C | 23.9 - 55.6 µin/in-°F | Average value: 67.8 µm/m-°C Grade Count:5 |
| Thermal Conductivity | 0.190 - 0.225 W/m-K | 1.32 - 1.56 BTU-in/hr-ft²-°F | Average value: 0.202 W/m-K Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 98.9 °C | 140 - 210 °F | Average value: 70.6 °C Grade Count:10 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 90.0 °C | 131 - 194 °F | Average value: 65.1 °C Grade Count:13 |
| Vicat Softening Point | 73.0 - 85.0 °C | 163 - 185 °F | Average value: 79.2 °C Grade Count:5 |
| Glass Transition Temp, Tg | 79.0 - 81.1 °C | 174 - 178 °F | Average value: 80.0 °C Grade Count:5 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.300 - 1.00 % | 0.300 - 1.00 % | Average value: 0.680 % Grade Count:5 |
| Transmission, Visible | 82.0 - 91.0 % | 82.0 - 91.0 % | Average value: 88.0 % Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 45.0 - 249 °C | 113 - 480 °F | Average value: 171 °C Grade Count:5 |
| Die Temperature | 195 - 293 °C | 383 - 560 °F | Average value: 254 °C Grade Count:5 |
| Melt Temperature | 180 - 293 °C | 356 - 560 °F | Average value: 245 °C Grade Count:9 |
| Mold Temperature | 12.0 - 70.0 °C | 53.6 - 158 °F | Average value: 31.9 °C Grade Count:4 |
| Drying Temperature | 65.0 - 102 °C | 149 - 216 °F | Average value: 71.5 °C Grade Count:7 |
| Dry Time | 4.00 - 12.0 hour | 4.00 - 12.0 hour | Average value: 4.86 hour Grade Count:7 |
| Moisture Content | 0.0200 % | 0.0200 % | Average value: 0.0200 % Grade Count:4 |
| Dew Point | -33.9 °C | -29.0 °F | Average value: -33.9 °C Grade Count:4 |