- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.69
- 断裂伸长率 [%]: 166.2
- 弯曲模量 [MPa]: 9.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | (24 hr); ASTM D570 |
| Moisture Absorption at Equilibrium | 0.24 % | 0.24 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 112.4 MPa | 16300 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 166.2 MPa | 24110 psi | ASTM D790 |
| Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 25.2 kV/mm | 640 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.5 µm/m-°C @Temperature 20.0 °C | 10.3 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | ASTM D648 |
| Vicat Softening Point | >= 225 °C | >= 437 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.125 in; Albis Internal Test |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 257 - 277 °C | 495 - 531 °F | Injection |
| Mold Temperature | 91.0 - 121 °C | 196 - 250 °F | |