- 缺口冲击强度: 0.908
- 弯曲模量 [MPa]: 9.65
- 热变形温度 [℃]: 246.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0019 cm/cm @Thickness 3.175 mm | 0.0019 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 221 MPa | 32000 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 438 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |