- 密度 [g/cm3]: 1.61
- 缺口冲击强度: 0.59
- 弯曲强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 11.2
- 硬度: 118.0
- 热变形温度 [℃]: 243.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 11.2 GPa | 1620 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.38 J/cm | 8.21 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 258 - 268 °C | 496 - 514 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 296 - 304 °C | 565 - 579 °F | Approximate middle barrel temperature range |