- 密度 [g/cm3]: 1.424
- 缺口冲击强度: 0.55
- 弯曲强度 [MPa]: 115.0
- 弯曲模量 [MPa]: 8.76
- 硬度: 118.0
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.424 g/cc | 0.05145 lb/in³ | Melt; ISO 1183 | ||
| 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 | |||
| Viscosity Measurement | 0.55 | 0.55 | Inherent Viscosity | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 0.2 in/min; ASTM Test | ||
| 45.0 MPa @Temperature 120 °C | 6530 psi @Temperature 248 °F | ISO Data | |||
| 45.0 MPa @Temperature 120 °C | 6530 psi @Temperature 248 °F | ASTM Test | |||
| 60.0 MPa @Temperature 80.0 °C | 8700 psi @Temperature 176 °F | ASTM Test | |||
| 60.0 MPa @Temperature 80.0 °C | 8700 psi @Temperature 176 °F | ISO Data | |||
| 145 MPa @Temperature -40.0 °C | 21000 psi @Temperature -40.0 °F | ASTM Test | |||
| 145 MPa @Temperature -40.0 °C | 21000 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 0.2 in/min; ASTM Test | ||
| 2.0 % | 2.0 % | 5mm/min; ISO 527 | |||
| 1.6 % @Temperature -40.0 °C | 1.6 % @Temperature -40.0 °F | ISO Data | |||
| 1.6 % @Temperature -40.0 °C | 1.6 % @Temperature -40.0 °F | ASTM Test | |||
| 6.3 % @Temperature 80.0 °C | 6.3 % @Temperature 176 °F | ASTM Test | |||
| 6.3 % @Temperature 80.0 °C | 6.3 % @Temperature 176 °F | ISO Data | |||
| 8.1 % @Temperature 120 °C | 8.1 % @Temperature 248 °F | ISO Data | |||
| 8.1 % @Temperature 120 °C | 8.1 % @Temperature 248 °F | ASTM Test | |||
| Tensile Modulus | 11.7 GPa | 1700 ksi | 1mm/min; ISO 527 | ||
| 2.59 GPa @Temperature 120 °C | 376 ksi @Temperature 248 °F | ISO Data | |||
| 4.12 GPa @Temperature 80.0 °C | 598 ksi @Temperature 176 °F | ISO Data | |||
| 12.27 GPa @Temperature -40.0 °C | 1780 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 180 MPa | 26100 psi | ASTM Test | ||
| Flexural Modulus | 8.76 GPa | 1270 ksi | ISO Data | ||
| 9.05 GPa | 1310 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.550 J/cm @Thickness 3.17 mm | 1.03 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 | ||
| 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 22.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 12.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Specific Heat Capacity | 1.906 J/g-°C | 0.4555 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.306 W/m-K | 2.12 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM Test | ||
| 210 °C | 410 °F | ISO 75 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Injection Velocity | 115 mm/sec | 4.53 in/sec | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-112 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||