- 熔体流动速率 [g/10min]: 8.04
- 密度 [g/cm3]: 1.34
- 拉伸强度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | Humidity Absorption; Sim. to ISO 62 | ||
| Melt Flow | 8.04 g/10 min @Load 2.16 kg, Temperature 250 °C | 8.04 g/10 min @Load 4.76 lb, Temperature 482 °F | Calculated from Volume Flow Rate of 6 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-1/-2 | ||
| Charpy Impact, Notched | 0.650 J/cm² @Temperature 23.0 °C | 3.09 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC 0; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 255 °C | 491 °F | 10°C/min; ISO 11357-1/-3 | ||
| UL RTI, Electrical | 75.0 °C @Thickness 0.930 mm | 167 °F @Thickness 0.0366 in | UL746B | ||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.930 mm | 167 °F @Thickness 0.0366 in | UL746B | ||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness 0.930 mm | 167 °F @Thickness 0.0366 in | UL746B | ||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | UL746B | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Oxygen Index | 25 % | 25 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Other Extrusion | Yes | ||||
| Profile Extrusion | Yes | ||||
| Sheet Extrusion | Yes | ||||
| Without Fillers | Yes | ||||