- 熔体流动速率 [g/10min]: 6.2
- 缺口冲击强度: 6.94
- 拉伸强度 [MPa]: 51.7
- 弯曲模量 [MPa]: 1.998
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 6.2 g/10 min @Load 3.80 kg, Temperature 300 °C | 6.2 g/10 min @Load 8.38 lb, Temperature 572 °F | ASTM D1238 |
| 26.2 g/10 min @Load 5.00 kg, Temperature 260 °C | 26.2 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 73.0 MPa | 10600 psi | chs 0.05 in/min; at yield; ASTM D790 |
| Flexural Modulus | 1.998 GPa | 289.8 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 6.94 J/cm @Thickness 3.17 mm | 13.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 161 °C @Load 1.00 kg, Thickness 3.17 mm | 322 °F @Load 2.20 lb, Thickness 0.125 in | ASTM D1527 |