  4. DuPont Performance Polymers Rynite® 540SUV BK544 PET

DuPont Performance Polymers Rynite® 540SUV BK544 PET

DuPont Performance Polymers Rynite® 540SUV BK544 PET 物性表: DuPont Performance Polymers Rynite® 540SUV BK544 PET物性表及特性介绍,DuPont Performance Polymers Rynite® 540SUV BK544 PET注塑参数详情,如需DuPont Performance Polymers Rynite® 540SUV BK544 PET下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.64
 
Physical PropertiesMetricEnglishComments
Density 1.64 g/cc0.0592 lb/in³ISO 1183
Filler Content 40 %40 %
Linear Mold Shrinkage, Flow 0.0020 cm/cm
@Thickness 2.00 mm		0.0020 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 162 MPa
@Temperature 23.0 °C		23500 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  0.700 MPa
@Strain 0.000 %,
Temperature 150 °C		102 psi
@Strain 0.000 %,
Temperature 302 °F		ISO 11403-1/-2
 1.08 MPa
@Strain 0.000 %,
Temperature 120 °C		157 psi
@Strain 0.000 %,
Temperature 248 °F		ISO 11403-1/-2
 1.49 MPa
@Strain 0.000 %,
Temperature 90.0 °C		216 psi
@Strain 0.000 %,
Temperature 194 °F		ISO 11403-1/-2
 1.65 MPa
@Strain 0.0500 %,
Temperature 120 °C		239 psi
@Strain 0.0500 %,
Temperature 248 °F		ISO 11403-1/-2
 1.83 MPa
@Strain 0.000 %,
Temperature 60.0 °C		265 psi
@Strain 0.000 %,
Temperature 140 °F		ISO 11403-1/-2
 1.85 MPa
@Strain 0.000 %,
Temperature 40.0 °C		268 psi
@Strain 0.000 %,
Temperature 104 °F		ISO 11403-1/-2
 1.89 MPa
@Strain 0.000 %,
Temperature 23.0 °C		274 psi
@Strain 0.000 %,
Temperature 73.4 °F		ISO 11403-1/-2
 2.05 MPa
@Strain 0.0600 %,
Temperature 90.0 °C		297 psi
@Strain 0.0600 %,
Temperature 194 °F		ISO 11403-1/-2
 2.39 MPa
@Strain 0.000 %,
Temperature 0.000 °C		347 psi
@Strain 0.000 %,
Temperature 32.0 °F		ISO 11403-1/-2
 2.42 MPa
@Strain 0.000 %,
Temperature -20.0 °C		351 psi
@Strain 0.000 %,
Temperature -4.00 °F		ISO 11403-1/-2
 2.46 MPa
@Strain 0.000 %,
Temperature -40.0 °C		357 psi
@Strain 0.000 %,
Temperature -40.0 °F		ISO 11403-1/-2
 2.65 MPa
@Strain 0.0400 %,
Temperature 60.0 °C		384 psi
@Strain 0.0400 %,
Temperature 140 °F		ISO 11403-1/-2
 2.79 MPa
@Strain 0.0400 %,
Temperature 40.0 °C		405 psi
@Strain 0.0400 %,
Temperature 104 °F		ISO 11403-1/-2
 2.89 MPa
@Strain 0.0400 %,
Temperature 23.0 °C		419 psi
@Strain 0.0400 %,
Temperature 73.4 °F		ISO 11403-1/-2
 3.01 MPa
@Strain 0.0700 %,
Temperature 150 °C		437 psi
@Strain 0.0700 %,
Temperature 302 °F		ISO 11403-1/-2
 3.13 MPa
@Strain 0.0400 %,
Temperature 0.000 °C		454 psi
@Strain 0.0400 %,
Temperature 32.0 °F		ISO 11403-1/-2
 3.85 MPa
@Strain 0.0400 %,
Temperature -20.0 °C		558 psi
@Strain 0.0400 %,
Temperature -4.00 °F		ISO 11403-1/-2
 4.10 MPa
@Strain 0.0400 %,
Temperature -40.0 °C		595 psi
@Strain 0.0400 %,
Temperature -40.0 °F		ISO 11403-1/-2
 4.63 MPa
@Strain 0.110 %,
Temperature 120 °C		672 psi
@Strain 0.110 %,
Temperature 248 °F		ISO 11403-1/-2
 5.07 MPa
@Strain 0.130 %,
Temperature 150 °C		735 psi
@Strain 0.130 %,
Temperature 302 °F		ISO 11403-1/-2
 5.63 MPa
@Strain 0.100 %,
Temperature 90.0 °C		817 psi
@Strain 0.100 %,
Temperature 194 °F		ISO 11403-1/-2
 6.08 MPa
@Strain 0.0800 %,
Temperature 60.0 °C		882 psi
@Strain 0.0800 %,
Temperature 140 °F		ISO 11403-1/-2
 6.18 MPa
@Strain 0.0700 %,
Temperature 40.0 °C		896 psi
@Strain 0.0700 %,
Temperature 104 °F		ISO 11403-1/-2
 6.38 MPa
@Strain 0.0700 %,
Temperature 23.0 °C		925 psi
@Strain 0.0700 %,
Temperature 73.4 °F		ISO 11403-1/-2
 6.48 MPa
@Strain 0.0700 %,
Temperature 0.000 °C		940 psi
@Strain 0.0700 %,
Temperature 32.0 °F		ISO 11403-1/-2
 6.93 MPa
@Strain 0.0700 %,
Temperature -20.0 °C		1010 psi
@Strain 0.0700 %,
Temperature -4.00 °F		ISO 11403-1/-2
 7.11 MPa
@Strain 0.190 %,
Temperature 150 °C		1030 psi
@Strain 0.190 %,
Temperature 302 °F		ISO 11403-1/-2
 7.73 MPa
@Strain 0.0700 %,
Temperature -40.0 °C		1120 psi
@Strain 0.0700 %,
Temperature -40.0 °F		ISO 11403-1/-2
 8.94 MPa
@Strain 0.170 %,
Temperature 120 °C		1300 psi
@Strain 0.170 %,
Temperature 248 °F		ISO 11403-1/-2
 9.13 MPa
@Strain 0.150 %,
Temperature 90.0 °C		1320 psi
@Strain 0.150 %,
Temperature 194 °F		ISO 11403-1/-2
 9.40 MPa
@Strain 0.260 %,
Temperature 150 °C		1360 psi
@Strain 0.260 %,
Temperature 302 °F		ISO 11403-1/-2
 10.03 MPa
@Strain 0.120 %,
Temperature 60.0 °C		1455 psi
@Strain 0.120 %,
Temperature 140 °F		ISO 11403-1/-2
 10.16 MPa
@Strain 0.110 %,
Temperature 40.0 °C		1474 psi
@Strain 0.110 %,
Temperature 104 °F		ISO 11403-1/-2
 10.36 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1503 psi
@Strain 0.100 %,
Temperature 73.4 °F		ISO 11403-1/-2
 10.93 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1585 psi
@Strain 0.100 %,
Temperature 32.0 °F		ISO 11403-1/-2
 11.23 MPa
@Strain 0.230 %,
Temperature 120 °C		1629 psi
@Strain 0.230 %,
Temperature 248 °F		ISO 11403-1/-2
 11.91 MPa
@Strain 0.100 %,
Temperature -20.0 °C		1727 psi
@Strain 0.100 %,
Temperature -4.00 °F		ISO 11403-1/-2
 12.71 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1843 psi
@Strain 0.100 %,
Temperature -40.0 °F		ISO 11403-1/-2
 13.67 MPa
@Strain 0.200 %,
Temperature 90.0 °C		1983 psi
@Strain 0.200 %,
Temperature 194 °F		ISO 11403-1/-2
 14.81 MPa
@Strain 0.150 %,
Temperature 60.0 °C		2148 psi
@Strain 0.150 %,
Temperature 140 °F		ISO 11403-1/-2
 14.93 MPa
@Strain 0.140 %,
Temperature 40.0 °C		2165 psi
@Strain 0.140 %,
Temperature 104 °F		ISO 11403-1/-2
 15.13 MPa
@Strain 0.130 %,
Temperature 23.0 °C		2194 psi
@Strain 0.130 %,
Temperature 73.4 °F		ISO 11403-1/-2
 15.43 MPa
@Strain 0.130 %,
Temperature 0.000 °C		2238 psi
@Strain 0.130 %,
Temperature 32.0 °F		ISO 11403-1/-2
 16.34 MPa
@Strain 0.250 %,
Temperature 90.0 °C		2370 psi
@Strain 0.250 %,
Temperature 194 °F		ISO 11403-1/-2
 16.75 MPa
@Strain 0.130 %,
Temperature -20.0 °C		2429 psi
@Strain 0.130 %,
Temperature -4.00 °F		ISO 11403-1/-2
 17.77 MPa
@Strain 0.130 %,
Temperature -40.0 °C		2577 psi
@Strain 0.130 %,
Temperature -40.0 °F		ISO 11403-1/-2
 18.24 MPa
@Strain 0.580 %,
Temperature 150 °C		2645 psi
@Strain 0.580 %,
Temperature 302 °F		ISO 11403-1/-2
 18.64 MPa
@Strain 0.400 %,
Temperature 120 °C		2704 psi
@Strain 0.400 %,
Temperature 248 °F		ISO 11403-1/-2
 19.06 MPa
@Strain 0.190 %,
Temperature 60.0 °C		2764 psi
@Strain 0.190 %,
Temperature 140 °F		ISO 11403-1/-2
 19.17 MPa
@Strain 0.170 %,
Temperature 40.0 °C		2780 psi
@Strain 0.170 %,
Temperature 104 °F		ISO 11403-1/-2
 19.37 MPa
@Strain 0.160 %,
Temperature 23.0 °C		2809 psi
@Strain 0.160 %,
Temperature 73.4 °F		ISO 11403-1/-2
 19.97 MPa
@Strain 0.160 %,
Temperature 0.000 °C		2896 psi
@Strain 0.160 %,
Temperature 32.0 °F		ISO 11403-1/-2
 21.47 MPa
@Strain 0.170 %,
Temperature -20.0 °C		3114 psi
@Strain 0.170 %,
Temperature -4.00 °F		ISO 11403-1/-2
 22.61 MPa
@Strain 0.160 %,
Temperature -40.0 °C		3279 psi
@Strain 0.160 %,
Temperature -40.0 °F		ISO 11403-1/-2
 23.02 MPa
@Strain 0.220 %,
Temperature 60.0 °C		3339 psi
@Strain 0.220 %,
Temperature 140 °F		ISO 11403-1/-2
 23.79 MPa
@Strain 0.200 %,
Temperature 40.0 °C		3450 psi
@Strain 0.200 %,
Temperature 104 °F		ISO 11403-1/-2
 23.89 MPa
@Strain 0.190 %,
Temperature 23.0 °C		3465 psi
@Strain 0.190 %,
Temperature 73.4 °F		ISO 11403-1/-2
 24.29 MPa
@Strain 0.200 %,
Temperature 0.000 °C		3523 psi
@Strain 0.200 %,
Temperature 32.0 °F		ISO 11403-1/-2
 24.82 MPa
@Strain 0.930 %,
Temperature 150 °C		3600 psi
@Strain 0.930 %,
Temperature 302 °F		ISO 11403-1/-2
 26.03 MPa
@Strain 0.200 %,
Temperature -20.0 °C		3775 psi
@Strain 0.200 %,
Temperature -4.00 °F		ISO 11403-1/-2
 26.13 MPa
@Strain 0.220 %,
Temperature 40.0 °C		3790 psi
@Strain 0.220 %,
Temperature 104 °F		ISO 11403-1/-2
 26.43 MPa
@Strain 0.220 %,
Temperature 23.0 °C		3833 psi
@Strain 0.220 %,
Temperature 73.4 °F		ISO 11403-1/-2
 26.85 MPa
@Strain 0.260 %,
Temperature 60.0 °C		3894 psi
@Strain 0.260 %,
Temperature 140 °F		ISO 11403-1/-2
 27.1 MPa
@Strain 0.180 %,
Temperature -40.0 °C		3930 psi
@Strain 0.180 %,
Temperature -40.0 °F		ISO 11403-1/-2
 27.69 MPa
@Strain 0.690 %,
Temperature 120 °C		4016 psi
@Strain 0.690 %,
Temperature 248 °F		ISO 11403-1/-2
 28.43 MPa
@Strain 0.230 %,
Temperature 0.000 °C		4123 psi
@Strain 0.230 %,
Temperature 32.0 °F		ISO 11403-1/-2
 29.07 MPa
@Strain 0.470 %,
Temperature 90.0 °C		4216 psi
@Strain 0.470 %,
Temperature 194 °F		ISO 11403-1/-2
 29.81 MPa
@Strain 1.27 %,
Temperature 150 °C		4324 psi
@Strain 1.27 %,
Temperature 302 °F		ISO 11403-1/-2
 30.44 MPa
@Strain 0.230 %,
Temperature -20.0 °C		4415 psi
@Strain 0.230 %,
Temperature -4.00 °F		ISO 11403-1/-2
 32.08 MPa
@Strain 0.210 %,
Temperature -40.0 °C		4653 psi
@Strain 0.210 %,
Temperature -40.0 °F		ISO 11403-1/-2
 32.32 MPa
@Strain 0.270 %,
Temperature 40.0 °C		4688 psi
@Strain 0.270 %,
Temperature 104 °F		ISO 11403-1/-2
 33.56 MPa
@Strain 0.250 %,
Temperature 23.0 °C		4867 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 11403-1/-2
 33.95 MPa
@Strain 1.63 %,
Temperature 150 °C		4924 psi
@Strain 1.63 %,
Temperature 302 °F		ISO 11403-1/-2
 34.75 MPa
@Strain 0.990 %,
Temperature 120 °C		5040 psi
@Strain 0.990 %,
Temperature 248 °F		ISO 11403-1/-2
 36.64 MPa
@Strain 0.240 %,
Temperature -40.0 °C		5314 psi
@Strain 0.240 %,
Temperature -40.0 °F		ISO 11403-1/-2
 37.1 MPa
@Strain 1.99 %,
Temperature 150 °C		5380 psi
@Strain 1.99 %,
Temperature 302 °F		ISO 11403-1/-2
 37.99 MPa
@Strain 0.300 %,
Temperature 0.000 °C		5510 psi
@Strain 0.300 %,
Temperature 32.0 °F		ISO 11403-1/-2
 38.61 MPa
@Strain 0.700 %,
Temperature 90.0 °C		5600 psi
@Strain 0.700 %,
Temperature 194 °F		ISO 11403-1/-2
 39.24 MPa
@Strain 0.390 %,
Temperature 60.0 °C		5691 psi
@Strain 0.390 %,
Temperature 140 °F		ISO 11403-1/-2
 39.64 MPa
@Strain 1.27 %,
Temperature 120 °C		5749 psi
@Strain 1.27 %,
Temperature 248 °F		ISO 11403-1/-2
 39.72 MPa
@Strain 2.33 %,
Temperature 150 °C		5761 psi
@Strain 2.33 %,
Temperature 302 °F		ISO 11403-1/-2
 39.84 MPa
@Strain 0.290 %,
Temperature -20.0 °C		5778 psi
@Strain 0.290 %,
Temperature -4.00 °F		ISO 11403-1/-2
 42.05 MPa
@Strain 2.69 %,
Temperature 150 °C		6099 psi
@Strain 2.69 %,
Temperature 302 °F		ISO 11403-1/-2
 43.41 MPa
@Strain 0.370 %,
Temperature 40.0 °C		6296 psi
@Strain 0.370 %,
Temperature 104 °F		ISO 11403-1/-2
 43.75 MPa
@Strain 1.55 %,
Temperature 120 °C		6345 psi
@Strain 1.55 %,
Temperature 248 °F		ISO 11403-1/-2
 44.19 MPa
@Strain 3.06 %,
Temperature 150 °C		6409 psi
@Strain 3.06 %,
Temperature 302 °F		ISO 11403-1/-2
 45.46 MPa
@Strain 0.900 %,
Temperature 90.0 °C		6593 psi
@Strain 0.900 %,
Temperature 194 °F		ISO 11403-1/-2
 46.09 MPa
@Strain 3.43 %,
Temperature 150 °C		6685 psi
@Strain 3.43 %,
Temperature 302 °F		ISO 11403-1/-2
 47.35 MPa
@Strain 1.85 %,
Temperature 120 °C		6868 psi
@Strain 1.85 %,
Temperature 248 °F		ISO 11403-1/-2
 47.81 MPa
@Strain 3.80 %,
Temperature 150 °C		6934 psi
@Strain 3.80 %,
Temperature 302 °F		ISO 11403-1/-2
 47.9 MPa
@Strain 0.500 %,
Temperature 60.0 °C		6950 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 11403-1/-2
 49.24 MPa
@Strain 0.310 %,
Temperature -40.0 °C		7142 psi
@Strain 0.310 %,
Temperature -40.0 °F		ISO 11403-1/-2
 49.38 MPa
@Strain 4.18 %,
Temperature 150 °C		7162 psi
@Strain 4.18 %,
Temperature 302 °F		ISO 11403-1/-2
 50.4 MPa
@Strain 2.15 %,
Temperature 120 °C		7310 psi
@Strain 2.15 %,
Temperature 248 °F		ISO 11403-1/-2
 50.85 MPa
@Strain 4.55 %,
Temperature 150 °C		7375 psi
@Strain 4.55 %,
Temperature 302 °F		ISO 11403-1/-2
 51.14 MPa
@Strain 1.11 %,
Temperature 90.0 °C		7417 psi
@Strain 1.11 %,
Temperature 194 °F		ISO 11403-1/-2
 51.17 MPa
@Strain 0.390 %,
Temperature 23.0 °C		7422 psi
@Strain 0.390 %,
Temperature 73.4 °F		ISO 11403-1/-2
 52.18 MPa
@Strain 4.95 %,
Temperature 150 °C		7568 psi
@Strain 4.95 %,
Temperature 302 °F		ISO 11403-1/-2
 52.48 MPa
@Strain 0.450 %,
Temperature 40.0 °C		7612 psi
@Strain 0.450 %,
Temperature 104 °F		ISO 11403-1/-2
 53.09 MPa
@Strain 2.46 %,
Temperature 120 °C		7700 psi
@Strain 2.46 %,
Temperature 248 °F		ISO 11403-1/-2
 53.4 MPa
@Strain 5.35 %,
Temperature 150 °C		7750 psi
@Strain 5.35 %,
Temperature 302 °F		ISO 11403-1/-2
 54.55 MPa
@Strain 5.73 %,
Temperature 150 °C		7912 psi
@Strain 5.73 %,
Temperature 302 °F		ISO 11403-1/-2
 55.48 MPa
@Strain 2.79 %,
Temperature 120 °C		8047 psi
@Strain 2.79 %,
Temperature 248 °F		ISO 11403-1/-2
 55.56 MPa
@Strain 6.11 %,
Temperature 150 °C		8058 psi
@Strain 6.11 %,
Temperature 302 °F		ISO 11403-1/-2
 56.06 MPa
@Strain 0.610 %,
Temperature 60.0 °C		8131 psi
@Strain 0.610 %,
Temperature 140 °F		ISO 11403-1/-2
 56.24 MPa
@Strain 1.33 %,
Temperature 90.0 °C		8157 psi
@Strain 1.33 %,
Temperature 194 °F		ISO 11403-1/-2
 56.25 MPa
@Strain 0.430 %,
Temperature 0.000 °C		8158 psi
@Strain 0.430 %,
Temperature 32.0 °F		ISO 11403-1/-2
 56.48 MPa
@Strain 6.49 %,
Temperature 150 °C		8192 psi
@Strain 6.49 %,
Temperature 302 °F		ISO 11403-1/-2
 57.33 MPa
@Strain 6.91 %,
Temperature 150 °C		8315 psi
@Strain 6.91 %,
Temperature 302 °F		ISO 11403-1/-2
 57.56 MPa
@Strain 0.410 %,
Temperature -20.0 °C		8348 psi
@Strain 0.410 %,
Temperature -4.00 °F		ISO 11403-1/-2
 57.7 MPa
@Strain 3.14 %,
Temperature 120 °C		8370 psi
@Strain 3.14 %,
Temperature 248 °F		ISO 11403-1/-2
 58.09 MPa
@Strain 7.35 %,
Temperature 150 °C		8425 psi
@Strain 7.35 %,
Temperature 302 °F		ISO 11403-1/-2
 58.2 MPa
@Strain 7.82 %,
Temperature 150 °C		8440 psi
@Strain 7.82 %,
Temperature 302 °F		ISO 11403-1/-2
 59.63 MPa
@Strain 3.48 %,
Temperature 120 °C		8649 psi
@Strain 3.48 %,
Temperature 248 °F		ISO 11403-1/-2
 60.77 MPa
@Strain 0.530 %,
Temperature 40.0 °C		8814 psi
@Strain 0.530 %,
Temperature 104 °F		ISO 11403-1/-2
 60.91 MPa
@Strain 1.57 %,
Temperature 90.0 °C		8834 psi
@Strain 1.57 %,
Temperature 194 °F		ISO 11403-1/-2
 61.41 MPa
@Strain 3.85 %,
Temperature 120 °C		8907 psi
@Strain 3.85 %,
Temperature 248 °F		ISO 11403-1/-2
 62.04 MPa
@Strain 0.400 %,
Temperature -40.0 °C		8998 psi
@Strain 0.400 %,
Temperature -40.0 °F		ISO 11403-1/-2
 62.17 MPa
@Strain 0.480 %,
Temperature 23.0 °C		9017 psi
@Strain 0.480 %,
Temperature 73.4 °F		ISO 11403-1/-2
 63.05 MPa
@Strain 4.22 %,
Temperature 120 °C		9145 psi
@Strain 4.22 %,
Temperature 248 °F		ISO 11403-1/-2
 63.79 MPa
@Strain 0.730 %,
Temperature 60.0 °C		9252 psi
@Strain 0.730 %,
Temperature 140 °F		ISO 11403-1/-2
 64.41 MPa
@Strain 4.55 %,
Temperature 120 °C		9342 psi
@Strain 4.55 %,
Temperature 248 °F		ISO 11403-1/-2
 65.07 MPa
@Strain 1.82 %,
Temperature 90.0 °C		9438 psi
@Strain 1.82 %,
Temperature 194 °F		ISO 11403-1/-2
 65.72 MPa
@Strain 4.96 %,
Temperature 120 °C		9532 psi
@Strain 4.96 %,
Temperature 248 °F		ISO 11403-1/-2
 66.89 MPa
@Strain 5.33 %,
Temperature 120 °C		9702 psi
@Strain 5.33 %,
Temperature 248 °F		ISO 11403-1/-2
 67.98 MPa
@Strain 5.74 %,
Temperature 120 °C		9860 psi
@Strain 5.74 %,
Temperature 248 °F		ISO 11403-1/-2
 68.78 MPa
@Strain 2.09 %,
Temperature 90.0 °C		9976 psi
@Strain 2.09 %,
Temperature 194 °F		ISO 11403-1/-2
 68.87 MPa
@Strain 0.610 %,
Temperature 40.0 °C		9989 psi
@Strain 0.610 %,
Temperature 104 °F		ISO 11403-1/-2
 68.89 MPa
@Strain 6.14 %,
Temperature 120 °C		9992 psi
@Strain 6.14 %,
Temperature 248 °F		ISO 11403-1/-2
 69.36 MPa
@Strain 0.540 %,
Temperature 0.000 °C		10060 psi
@Strain 0.540 %,
Temperature 32.0 °F		ISO 11403-1/-2
 69.55 MPa
@Strain 6.98 %,
Temperature 120 °C		10090 psi
@Strain 6.98 %,
Temperature 248 °F		ISO 11403-1/-2
 69.65 MPa
@Strain 6.55 %,
Temperature 120 °C		10100 psi
@Strain 6.55 %,
Temperature 248 °F		ISO 11403-1/-2
 70.67 MPa
@Strain 0.510 %,
Temperature -20.0 °C		10250 psi
@Strain 0.510 %,
Temperature -4.00 °F		ISO 11403-1/-2
 71.66 MPa
@Strain 0.870 %,
Temperature 60.0 °C		10390 psi
@Strain 0.870 %,
Temperature 140 °F		ISO 11403-1/-2
 71.9 MPa
@Strain 0.570 %,
Temperature 23.0 °C		10400 psi
@Strain 0.570 %,
Temperature 73.4 °F		ISO 11403-1/-2
 71.98 MPa
@Strain 2.36 %,
Temperature 90.0 °C		10440 psi
@Strain 2.36 %,
Temperature 194 °F		ISO 11403-1/-2
 72.86 MPa
@Strain 0.450 %,
Temperature -40.0 °C		10570 psi
@Strain 0.450 %,
Temperature -40.0 °F		ISO 11403-1/-2
 74.85 MPa
@Strain 2.66 %,
Temperature 90.0 °C		10860 psi
@Strain 2.66 %,
Temperature 194 °F		ISO 11403-1/-2
 77.37 MPa
@Strain 0.700 %,
Temperature 40.0 °C		11220 psi
@Strain 0.700 %,
Temperature 104 °F		ISO 11403-1/-2
 77.38 MPa
@Strain 2.97 %,
Temperature 90.0 °C		11220 psi
@Strain 2.97 %,
Temperature 194 °F		ISO 11403-1/-2
 78.72 MPa
@Strain 1.01 %,
Temperature 60.0 °C		11420 psi
@Strain 1.01 %,
Temperature 140 °F		ISO 11403-1/-2
 79.56 MPa
@Strain 3.29 %,
Temperature 90.0 °C		11540 psi
@Strain 3.29 %,
Temperature 194 °F		ISO 11403-1/-2
 79.96 MPa
@Strain 0.620 %,
Temperature 0.000 °C		11600 psi
@Strain 0.620 %,
Temperature 32.0 °F		ISO 11403-1/-2
 81.36 MPa
@Strain 0.650 %,
Temperature 23.0 °C		11800 psi
@Strain 0.650 %,
Temperature 73.4 °F		ISO 11403-1/-2
 81.51 MPa
@Strain 3.62 %,
Temperature 90.0 °C		11820 psi
@Strain 3.62 %,
Temperature 194 °F		ISO 11403-1/-2
 82.26 MPa
@Strain 0.600 %,
Temperature -20.0 °C		11930 psi
@Strain 0.600 %,
Temperature -4.00 °F		ISO 11403-1/-2
 83.22 MPa
@Strain 3.95 %,
Temperature 90.0 °C		12070 psi
@Strain 3.95 %,
Temperature 194 °F		ISO 11403-1/-2
 84.32 MPa
@Strain 0.520 %,
Temperature -40.0 °C		12230 psi
@Strain 0.520 %,
Temperature -40.0 °F		ISO 11403-1/-2
 84.63 MPa
@Strain 4.32 %,
Temperature 90.0 °C		12270 psi
@Strain 4.32 %,
Temperature 194 °F		ISO 11403-1/-2
 85.49 MPa
@Strain 1.17 %,
Temperature 60.0 °C		12400 psi
@Strain 1.17 %,
Temperature 140 °F		ISO 11403-1/-2
 85.72 MPa
@Strain 0.800 %,
Temperature 40.0 °C		12430 psi
@Strain 0.800 %,
Temperature 104 °F		ISO 11403-1/-2
 85.84 MPa
@Strain 4.71 %,
Temperature 90.0 °C		12450 psi
@Strain 4.71 %,
Temperature 194 °F		ISO 11403-1/-2
 86.88 MPa
@Strain 5.09 %,
Temperature 90.0 °C		12600 psi
@Strain 5.09 %,
Temperature 194 °F		ISO 11403-1/-2
 87.33 MPa
@Strain 5.93 %,
Temperature 90.0 °C		12670 psi
@Strain 5.93 %,
Temperature 194 °F		ISO 11403-1/-2
 87.62 MPa
@Strain 5.49 %,
Temperature 90.0 °C		12710 psi
@Strain 5.49 %,
Temperature 194 °F		ISO 11403-1/-2
 90.06 MPa
@Strain 0.710 %,
Temperature 0.000 °C		13060 psi
@Strain 0.710 %,
Temperature 32.0 °F		ISO 11403-1/-2
 90.46 MPa
@Strain 0.740 %,
Temperature 23.0 °C		13120 psi
@Strain 0.740 %,
Temperature 73.4 °F		ISO 11403-1/-2
 91.96 MPa
@Strain 1.35 %,
Temperature 60.0 °C		13340 psi
@Strain 1.35 %,
Temperature 140 °F		ISO 11403-1/-2
 93.71 MPa
@Strain 0.680 %,
Temperature -20.0 °C		13590 psi
@Strain 0.680 %,
Temperature -4.00 °F		ISO 11403-1/-2
 94.38 MPa
@Strain 0.920 %,
Temperature 40.0 °C		13690 psi
@Strain 0.920 %,
Temperature 104 °F		ISO 11403-1/-2
 95.95 MPa
@Strain 0.600 %,
Temperature -40.0 °C		13920 psi
@Strain 0.600 %,
Temperature -40.0 °F		ISO 11403-1/-2
 97.49 MPa
@Strain 1.55 %,
Temperature 60.0 °C		14140 psi
@Strain 1.55 %,
Temperature 140 °F		ISO 11403-1/-2
 99.27 MPa
@Strain 0.830 %,
Temperature 23.0 °C		14400 psi
@Strain 0.830 %,
Temperature 73.4 °F		ISO 11403-1/-2
 100.21 MPa
@Strain 0.800 %,
Temperature 0.000 °C		14534 psi
@Strain 0.800 %,
Temperature 32.0 °F		ISO 11403-1/-2
 102.36 MPa
@Strain 1.04 %,
Temperature 40.0 °C		14846 psi
@Strain 1.04 %,
Temperature 104 °F		ISO 11403-1/-2
 102.48 MPa
@Strain 1.78 %,
Temperature 60.0 °C		14863 psi
@Strain 1.78 %,
Temperature 140 °F		ISO 11403-1/-2
 104.85 MPa
@Strain 0.770 %,
Temperature -20.0 °C		15207 psi
@Strain 0.770 %,
Temperature -4.00 °F		ISO 11403-1/-2
 106.51 MPa
@Strain 2.00 %,
Temperature 60.0 °C		15448 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 11403-1/-2
 107.78 MPa
@Strain 0.670 %,
Temperature -40.0 °C		15632 psi
@Strain 0.670 %,
Temperature -40.0 °F		ISO 11403-1/-2
 107.87 MPa
@Strain 0.940 %,
Temperature 23.0 °C		15645 psi
@Strain 0.940 %,
Temperature 73.4 °F		ISO 11403-1/-2
 110.04 MPa
@Strain 2.28 %,
Temperature 60.0 °C		15960 psi
@Strain 2.28 %,
Temperature 140 °F		ISO 11403-1/-2
 110.26 MPa
@Strain 0.890 %,
Temperature 0.000 °C		15992 psi
@Strain 0.890 %,
Temperature 32.0 °F		ISO 11403-1/-2
 110.36 MPa
@Strain 1.18 %,
Temperature 40.0 °C		16006 psi
@Strain 1.18 %,
Temperature 104 °F		ISO 11403-1/-2
 112.72 MPa
@Strain 2.56 %,
Temperature 60.0 °C		16349 psi
@Strain 2.56 %,
Temperature 140 °F		ISO 11403-1/-2
 114.68 MPa
@Strain 2.86 %,
Temperature 60.0 °C		16633 psi
@Strain 2.86 %,
Temperature 140 °F		ISO 11403-1/-2
 115.9 MPa
@Strain 3.89 %,
Temperature 60.0 °C		16810 psi
@Strain 3.89 %,
Temperature 140 °F		ISO 11403-1/-2
 116.06 MPa
@Strain 3.19 %,
Temperature 60.0 °C		16833 psi
@Strain 3.19 %,
Temperature 140 °F		ISO 11403-1/-2
 116.09 MPa
@Strain 0.870 %,
Temperature -20.0 °C		16837 psi
@Strain 0.870 %,
Temperature -4.00 °F		ISO 11403-1/-2
 116.62 MPa
@Strain 1.04 %,
Temperature 23.0 °C		16914 psi
@Strain 1.04 %,
Temperature 73.4 °F		ISO 11403-1/-2
 116.86 MPa
@Strain 3.53 %,
Temperature 60.0 °C		16949 psi
@Strain 3.53 %,
Temperature 140 °F		ISO 11403-1/-2
 117.6 MPa
@Strain 1.33 %,
Temperature 40.0 °C		17060 psi
@Strain 1.33 %,
Temperature 104 °F		ISO 11403-1/-2
 119.7 MPa
@Strain 0.760 %,
Temperature -40.0 °C		17360 psi
@Strain 0.760 %,
Temperature -40.0 °F		ISO 11403-1/-2
 120.64 MPa
@Strain 0.990 %,
Temperature 0.000 °C		17497 psi
@Strain 0.990 %,
Temperature 32.0 °F		ISO 11403-1/-2
 124.08 MPa
@Strain 1.50 %,
Temperature 40.0 °C		17996 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 11403-1/-2
 124.59 MPa
@Strain 1.15 %,
Temperature 23.0 °C		18070 psi
@Strain 1.15 %,
Temperature 73.4 °F		ISO 11403-1/-2
 127.11 MPa
@Strain 0.960 %,
Temperature -20.0 °C		18436 psi
@Strain 0.960 %,
Temperature -4.00 °F		ISO 11403-1/-2
 129.68 MPa
@Strain 1.68 %,
Temperature 40.0 °C		18809 psi
@Strain 1.68 %,
Temperature 104 °F		ISO 11403-1/-2
 130.19 MPa
@Strain 1.10 %,
Temperature 0.000 °C		18882 psi
@Strain 1.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 131.99 MPa
@Strain 0.860 %,
Temperature -40.0 °C		19144 psi
@Strain 0.860 %,
Temperature -40.0 °F		ISO 11403-1/-2
 132.13 MPa
@Strain 1.28 %,
Temperature 23.0 °C		19164 psi
@Strain 1.28 %,
Temperature 73.4 °F		ISO 11403-1/-2
 134.57 MPa
@Strain 1.90 %,
Temperature 40.0 °C		19518 psi
@Strain 1.90 %,
Temperature 104 °F		ISO 11403-1/-2
 138.01 MPa
@Strain 1.06 %,
Temperature -20.0 °C		20017 psi
@Strain 1.06 %,
Temperature -4.00 °F		ISO 11403-1/-2
 138.3 MPa
@Strain 2.12 %,
Temperature 40.0 °C		20060 psi
@Strain 2.12 %,
Temperature 104 °F		ISO 11403-1/-2
 139.32 MPa
@Strain 1.42 %,
Temperature 23.0 °C		20207 psi
@Strain 1.42 %,
Temperature 73.4 °F		ISO 11403-1/-2
 139.85 MPa
@Strain 1.22 %,
Temperature 0.000 °C		20284 psi
@Strain 1.22 %,
Temperature 32.0 °F		ISO 11403-1/-2
 140.77 MPa
@Strain 2.40 %,
Temperature 40.0 °C		20417 psi
@Strain 2.40 %,
Temperature 104 °F		ISO 11403-1/-2
 141.6 MPa
@Strain 2.70 %,
Temperature 40.0 °C		20540 psi
@Strain 2.70 %,
Temperature 104 °F		ISO 11403-1/-2
 144.08 MPa
@Strain 0.960 %,
Temperature -40.0 °C		20897 psi
@Strain 0.960 %,
Temperature -40.0 °F		ISO 11403-1/-2
 146.03 MPa
@Strain 1.57 %,
Temperature 23.0 °C		21180 psi
@Strain 1.57 %,
Temperature 73.4 °F		ISO 11403-1/-2
 148.63 MPa
@Strain 1.33 %,
Temperature 0.000 °C		21557 psi
@Strain 1.33 %,
Temperature 32.0 °F		ISO 11403-1/-2
 148.82 MPa
@Strain 1.17 %,
Temperature -20.0 °C		21585 psi
@Strain 1.17 %,
Temperature -4.00 °F		ISO 11403-1/-2
 152.34 MPa
@Strain 1.74 %,
Temperature 23.0 °C		22095 psi
@Strain 1.74 %,
Temperature 73.4 °F		ISO 11403-1/-2
 156.09 MPa
@Strain 1.05 %,
Temperature -40.0 °C		22639 psi
@Strain 1.05 %,
Temperature -40.0 °F		ISO 11403-1/-2
 157.09 MPa
@Strain 1.45 %,
Temperature 0.000 °C		22784 psi
@Strain 1.45 %,
Temperature 32.0 °F		ISO 11403-1/-2
 157.49 MPa
@Strain 1.92 %,
Temperature 23.0 °C		22842 psi
@Strain 1.92 %,
Temperature 73.4 °F		ISO 11403-1/-2
 159.56 MPa
@Strain 1.28 %,
Temperature -20.0 °C		23142 psi
@Strain 1.28 %,
Temperature -4.00 °F		ISO 11403-1/-2
 161.59 MPa
@Strain 2.12 %,
Temperature 23.0 °C		23437 psi
@Strain 2.12 %,
Temperature 73.4 °F		ISO 11403-1/-2
 164.13 MPa
@Strain 2.40 %,
Temperature 23.0 °C		23805 psi
@Strain 2.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 165.02 MPa
@Strain 1.58 %,
Temperature 0.000 °C		23934 psi
@Strain 1.58 %,
Temperature 32.0 °F		ISO 11403-1/-2
 168.21 MPa
@Strain 1.16 %,
Temperature -40.0 °C		24397 psi
@Strain 1.16 %,
Temperature -40.0 °F		ISO 11403-1/-2
 170.42 MPa
@Strain 1.42 %,
Temperature -20.0 °C		24717 psi
@Strain 1.42 %,
Temperature -4.00 °F		ISO 11403-1/-2
 172.56 MPa
@Strain 1.73 %,
Temperature 0.000 °C		25028 psi
@Strain 1.73 %,
Temperature 32.0 °F		ISO 11403-1/-2
 179.83 MPa
@Strain 1.27 %,
Temperature -40.0 °C		26082 psi
@Strain 1.27 %,
Temperature -40.0 °F		ISO 11403-1/-2
 179.87 MPa
@Strain 1.89 %,
Temperature 0.000 °C		26088 psi
@Strain 1.89 %,
Temperature 32.0 °F		ISO 11403-1/-2
 180.68 MPa
@Strain 1.54 %,
Temperature -20.0 °C		26205 psi
@Strain 1.54 %,
Temperature -4.00 °F		ISO 11403-1/-2
 186.01 MPa
@Strain 2.06 %,
Temperature 0.000 °C		26979 psi
@Strain 2.06 %,
Temperature 32.0 °F		ISO 11403-1/-2
 190.22 MPa
@Strain 1.67 %,
Temperature -20.0 °C		27589 psi
@Strain 1.67 %,
Temperature -4.00 °F		ISO 11403-1/-2
 191.12 MPa
@Strain 2.25 %,
Temperature 0.000 °C		27720 psi
@Strain 2.25 %,
Temperature 32.0 °F		ISO 11403-1/-2
 191.29 MPa
@Strain 1.40 %,
Temperature -40.0 °C		27744 psi
@Strain 1.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 199.2 MPa
@Strain 1.82 %,
Temperature -20.0 °C		28890 psi
@Strain 1.82 %,
Temperature -4.00 °F		ISO 11403-1/-2
 202.01 MPa
@Strain 1.52 %,
Temperature -40.0 °C		29299 psi
@Strain 1.52 %,
Temperature -40.0 °F		ISO 11403-1/-2
 207.43 MPa
@Strain 1.97 %,
Temperature -20.0 °C		30085 psi
@Strain 1.97 %,
Temperature -4.00 °F		ISO 11403-1/-2
 212.16 MPa
@Strain 1.67 %,
Temperature -40.0 °C		30771 psi
@Strain 1.67 %,
Temperature -40.0 °F		ISO 11403-1/-2
 214.94 MPa
@Strain 2.14 %,
Temperature -20.0 °C		31174 psi
@Strain 2.14 %,
Temperature -4.00 °F		ISO 11403-1/-2
 221.48 MPa
@Strain 1.82 %,
Temperature -40.0 °C		32123 psi
@Strain 1.82 %,
Temperature -40.0 °F		ISO 11403-1/-2
Elongation at Break 2.3 %
@Temperature 23.0 °C		2.3 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 13.5 GPa
@Temperature 23.0 °C		1960 ksi
@Temperature 73.4 °F		ISO 527
Charpy Impact Unnotched 6.00 J/cm²
@Temperature 23.0 °C		28.6 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched 0.880 J/cm²
@Temperature 23.0 °C		4.19 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 80.0 °C		278 µin/in-°F
@Temperature 131 - 176 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 80.0 - 160 °C		278 µin/in-°F
@Temperature 176 - 320 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  75.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		41.7 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 75.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		41.7 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 85.0 µm/m-°C
@Temperature 80.0 - 160 °C		47.2 µin/in-°F
@Temperature 176 - 320 °F		ISO 11359-1/-2
 120 µm/m-°C
@Temperature 55.0 - 80.0 °C		66.7 µin/in-°F
@Temperature 131 - 176 °F		ISO 11359-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 249 °C480 °F10°C/min; ISO 11357-1/-3
 285 °C545 °FOptimum
 280 - 300 °C536 - 572 °F
Mold Temperature >= 95.0 °C>= 203 °F
 110 °C230 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AppearanceBlack Color
FillerGlass fiber
FormsPellets
GenericPET
Material StatusPreliminary Data
Part Marking Code>PET-GF40<ISO 11469
Processing MethodExtrusion
Product CategoryExtrusion Resins
 Glass Reinforced Resins
 Glass Reinforced Resins
 UV Resistant/Weatherable Resins
 UV Resistant/Weatherable Resins
Region Available - GlobalYes
Resin IdentificationPET-GF40ISO 1043
RoHS ComplianceContact Manufacturer

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38909.html

免责声明: 本文 DuPont Performance Polymers Rynite® 540SUV BK544 PET 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4