- 密度 [g/cm3]: 1.49
- 缺口冲击强度: 13.0
- 弯曲模量 [MPa]: 7.962
- 热变形温度 [℃]: 237.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 55.0 MPa @Temperature 150 °C | 7980 psi @Temperature 302 °F | ISO 527 | ||
| 71.0 MPa @Temperature 90.0 °C | 10300 psi @Temperature 194 °F | ISO 527 | |||
| 127 MPa @Temperature 23.0 °C | 18400 psi @Temperature 73.4 °F | ISO 527 | |||
| 179 MPa @Temperature -40.0 °C | 26000 psi @Temperature -40.0 °F | ISO 527 | |||
| Elongation at Break | 2.6 % @Temperature -40.0 °C | 2.6 % @Temperature -40.0 °F | ISO 527 | ||
| 2.9 % @Temperature 23.0 °C | 2.9 % @Temperature 73.4 °F | ISO 527 | |||
| 9.7 % @Temperature 90.0 °C | 9.7 % @Temperature 194 °F | ISO 527 | |||
| 11 % @Temperature 150 °C | 11 % @Temperature 302 °F | ISO 527 | |||
| Tensile Modulus | 2.89 GPa @Temperature 150 °C | 419 ksi @Temperature 302 °F | ISO 527 | ||
| 4.02 GPa @Temperature 90.0 °C | 583 ksi @Temperature 194 °F | ISO 527 | |||
| 9.30 GPa @Temperature 23.0 °C | 1350 ksi @Temperature 73.4 °F | ISO 527 | |||
| 10.79 GPa @Temperature -40.0 °C | 1565 ksi @Temperature -40.0 °F | ISO 527 | |||
| Flexural Modulus | 7.962 GPa @Temperature 23.0 °C | 1155 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 6.40 J/cm² @Temperature 23.0 °C | 30.5 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 237 °C | 459 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Optimum | ||
| 270 - 290 °C | 518 - 554 °F | ||||
| Mold Temperature | >= 95.0 °C | >= 203 °F | |||
| 110 °C | 230 °F | Optimum | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Features | Creep Resistance, Good | ||||
| Dimensional Stability, Good | |||||
| Electrical Properties, Good | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Thermal Aging Resistance, Good | |||||
| Filler | Glass fiber reinforcement | ||||
| Glass Reinforced | |||||
| Generic | PET | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-IGF30< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Glass Reinforced Resins | ||||
| Toughened Resins | |||||
| Region Available - Americas | Yes | ||||
| Region Available - Asia/Pacific | Yes | ||||
| Region Available - Europe | Yes | ||||
| Resin Identification | PET-IGF30 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Automotive Applications | ||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Phenolic Replacement | |||||
| Structural Parts | |||||