- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.34
- 拉伸强度 [MPa]: 54.0
- 断裂伸长率 [%]: 76.0
- 弯曲模量 [MPa]: 2.40
- 硬度: 111.0
- 热变形温度 [℃]: 69.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Bulk Density | 0.803 g/cc | 0.0290 lb/in³ | Poured; ASTM D1895 | ||
| 0.881 g/cc | 0.0318 lb/in³ | Vibrated; ASTM D1895 | |||
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| 1.40 g/cc | 0.0506 lb/in³ | Crystalline Density; ASTM D1505 | |||
| Melt Density | 1.20 g/cc @Temperature 285 °C | 0.0434 lb/in³ @Temperature 545 °F | ASTM D1238 | ||
| Viscosity Measurement | 0.78 - 0.82 | 0.78 - 0.82 | Pellet, Intrinsic; VGAS-A-AN-G-V-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 111 | 111 | ASTM D785 | ||
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 527 | ||
| 31.0 MPa | 4500 psi | ASTM D638 | |||
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 | ||
| 55.0 MPa | 7980 psi | ASTM D638 | |||
| Elongation at Break | 114 % | 114 % | ISO 527 | ||
| 173 % | 173 % | ASTM D638 | |||
| Tensile Modulus | 2.30 GPa | 334 ksi | ASTM D638 | ||
| 2.332 GPa | 338.2 ksi | ISO 527 | |||
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 | ||
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.340 J/cm @Temperature -40.0 °C | 0.637 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.790 J/cm @Temperature 23.0 °C | 1.48 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Izod Impact, Unnotched | NB | NB | ASTM D4812 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 3.90 kJ/m² @Temperature -40.0 °C | 1.86 ft-lb/in² @Temperature -40.0 °F | ISO 180 | ||
| 6.80 kJ/m² @Temperature 23.0 °C | 3.24 ft-lb/in² @Temperature 73.4 °F | ISO 180 | |||
| Puncture Energy | 8.20 J @Thickness 2.70 mm, Temperature -40.0 °C | 6.05 ft-lb @Thickness 0.106 in, Temperature -40.0 °F | max load; ASTM D3763 | ||
| 31.0 J @Thickness 2.70 mm, Temperature 23.0 °C | 22.9 ft-lb @Thickness 0.106 in, Temperature 73.4 °F | max load; ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 61.0 J/g | 26.2 BTU/lb | ASTM E793 | ||
| Specific Heat Capacity | 1.20 J/g-°C | 0.287 BTU/lb-°F | ASTM E1269 | ||
| 1.40 J/g-°C @Temperature 80.0 °C | 0.335 BTU/lb-°F @Temperature 176 °F | ASTM E1269 | |||
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ASTM E1269 | |||
| 2.00 J/g-°C @Temperature 200 °C | 0.478 BTU/lb-°F @Temperature 392 °F | ASTM E1269 | |||
| 2.10 J/g-°C @Temperature 280 °C | 0.502 BTU/lb-°F @Temperature 536 °F | ASTM E1269 | |||
| Melting Point | 239 °C | 462 °F | Crystalline Peak Melting Point; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 | ||
| 69.0 °C | 156 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM D648 | ||
| 64.0 °C | 147 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Acetaldehyde | <1ppm | VKCA-A-AS-G-GC-0001 | |||
| Color, CIE a* | -3.5 to -0.5 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE b* | -2.5 to 1.5 | VGAS-A-AN-G-RS-001 | |||
| Color, CIE L* | 78 min | VGAS-A-AN-G-RS-001 | |||
| Fines, wt%, max | 0.05 | VGAS-A-AN-G-GA-1 | |||
| Pellet Shape | Rectangular 2x2x3 mm | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.