- 密度 [g/cm3]: 1.21
- 拉伸强度 [MPa]: 44.0
- 热变形温度 [℃]: 86.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 4.5 % | 4.5 % | |
| Tensile Modulus | 1.84 GPa | 267 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 9.00 J/cm² | 42.8 ft-lb/in² | Partial Break |
| 1.15 J/cm² @Temperature -30.0 °C | 5.47 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 62.0 µm/m-°C @Temperature 20.0 °C | 34.4 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 71.0 µm/m-°C @Temperature 20.0 °C | 39.4 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | |
| Vicat Softening Point | 90.0 °C | 194 °F | |
| Glass Transition Temp, Tg | 92.0 °C | 198 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |