- 密度 [g/cm3]: 1.74
- 缺口冲击强度: 13.0
- 弯曲模量 [MPa]: 17.0
- 热变形温度 [℃]: 252.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.150 % | 0.150 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 50.0 cm³/g | 50.0 cm³/g | ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 121 | 121 | ISO 2039-2 | ||
| Tensile Strength at Break | 185 MPa | 26800 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.50 % | 1.50 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 17.0 GPa | 2470 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 240 MPa | 34800 psi | ISO 178 | ||
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU | ||
| 3.10 J/cm² @Temperature -30.0 °C | 14.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA | ||
| 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.50 @Frequency 1.00e+6 Hz | 4.50 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 5.20 @Frequency 100 Hz | 5.20 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00300 @Frequency 100 Hz | 0.00300 @Frequency 100 Hz | IEC 60250 | ||
| 0.0165 @Frequency 1.00e+6 Hz | 0.0165 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 248 °C | 478 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 170 °C | 338 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 260 °C | 500 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL94 | |||
| Oxygen Index | 26.0 % | 26.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 135 - 145 °C | 275 - 293 °F | Cavity temperature | |||
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |||
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |||
| Zone 3 | 280 - 290 °C | 536 - 554 °F | |||
| Zone 4 | 280 - 290 °C | 536 - 554 °F | |||
| Die Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |||
| 270 - 290 °C | 518 - 554 °F | ||||
| Mold Temperature | 135 - 145 °C | 275 - 293 °F | |||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| Hold Pressure | 30.0 - 50.0 MPa | 4350 - 7250 psi | |||
| 60.0 - 90.0 MPa | 8700 - 13100 psi | ||||
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi | |||
| Screw Speed | 50.0 rpm @Diameter 55.0 mm | 50.0 rpm @Diameter 2.17 in | |||
| 65.0 rpm @Diameter 40.0 mm | 65.0 rpm @Diameter 1.57 in | ||||
| 80.0 rpm @Diameter 25.0 mm | 80.0 rpm @Diameter 0.984 in | ||||
| Hot-Working Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | fast | ||||
| Longer pre-drying times/storage | 100° C | <= 60 h | |||
| Nozzle Design | open design preferred | ||||
| Peripheral screw speed | max. 0.3 m/sec | ||||
| Processing Notes | Fast Injection Speed | ||||
| Maximum Barrel Residence Time 5-10 min | |||||