- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 0.06
- 缺口冲击强度: 2.5
- 弯曲模量 [MPa]: 2.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | Test Method A; ISO 1183:1987 | ||
| Water Absorption | 0.060 % @Temperature 23.0 °C, Time 86400 sec | 0.060 % @Temperature 73.4 °F, Time 24.0 hour | Immersion; ISO 62:1999 (modified) | ||
| Moisture Absorption at Equilibrium | 0.23 % | 0.23 % | 50% RH; ISO 62:1999 | ||
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62:1999 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Sample Type 1B, 50mm/min; ISO 527-1/2:1993 | ||
| Elongation at Break | >= 10 % | >= 10 % | Sample Type 1B, 50 mm/min; ISO 527-1/2:1993 | ||
| Modulus of Elasticity | 3.50 GPa | 508 ksi | Sample Type 1B, 50 mm/min; ISO 527-1/2:1993 | ||
| Flexural Strength | 95.0 MPa | 13800 psi | 1.5 mm/min; ISO 178:2001 | ||
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.5 mm/min; ISO 178:2001 | ||
| Compressive Strength | 100 MPa | 14500 psi | Sample Type B, 5 mm/min; ISO 604:2002 | ||
| Compressive Modulus | 2.70 GPa | 392 ksi | Sample Type A, 1 mm/min; ISO 604:2002 | ||
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | Sample Type A; ISO 180:2000 | ||
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | ISO 179-2:1999 | ||
| Coefficient of Friction, Dynamic | 0.19 @Pressure 1.75 MPa | 0.19 @Pressure 254 psi | 31.4 m/min | ||
| Limiting Pressure Velocity | 0.217 MPa-m/sec | 6200 psi-ft/min | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093:1980-01 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093:1980-01 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | IEC 60250:1969-01 | ||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | IEC 60250:1969-01 | |||
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | IEC 60243-1:1998-01 | ||
| Dissipation Factor | 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | IEC 60250:1969-01 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112:2003-01 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 67.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 37.2 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-2:1999 | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ISO 8301:1991 | ||
| Melting Point | 255 °C | 491 °F | |||
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous | ||
| 160 °C | 320 °F | Intermittent | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 | ||
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | Continuous | ||
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | ISO 11359-2:1999 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10:2003-08 | ||
| Descriptive Properties | |||||
| Color | Light Grey | ||||