- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.412
- 断裂伸长率 [%]: 63.7
- 弯曲强度 [MPa]: 69.6
- 弯曲模量 [MPa]: 3.14
- 硬度: 91.0
- 热变形温度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min @Temperature 275 °C | 25 g/10 min @Temperature 527 °F | DSC |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 91 | 91 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 69.6 MPa | 10100 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 60 % | 60 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 63.7 MPa | 9250 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 3.14 GPa | 455 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.412 J/cm | 0.771 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 400 µm/m-°C @Temperature 20.0 °C | 222 µin/in-°F @Temperature 68.0 °F | DIN 53752; ASTM D696 |
| Melting Point | 215 °C | 419 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |