- 密度 [g/cm3]: 1.4
- 缺口冲击强度: 0.5
- 弯曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 2.00 mm | 0.0060 in/in @Thickness 0.0787 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | ASTM D955 |
| Ash | 15 % | 15 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 150 MPa | 21800 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C | 0.937 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Nozzle Temperature | 275 - 295 °C | 527 - 563 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 95.0 - 120 °C | 203 - 248 °F | |