- 缺口冲击强度: 0.304
- 断裂伸长率 [%]: 90.2
- 弯曲模量 [MPa]: 3.63
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.015 cm/cm @Thickness 3.20 mm | 0.0070 - 0.015 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 53.0 MPa @Thickness 3.20 mm | 7690 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm | 3.0 % @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Flexural Yield Strength | 90.2 MPa @Thickness 3.20 mm | 13100 psi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Flexural Modulus | 3.63 GPa @Thickness 3.20 mm | 526 ksi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.304 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 0.569 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C @Thickness 6.40 mm | 374 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Nozzle Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Melt Temperature | 225 °C | 437 °F | @ Break; ASTM D3418 |
| 245 - 255 °C | 473 - 491 °F | Injection Molding | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |