- 密度 [g/cm3]: 1.64
- 吸水率 [%]: 0.06
- 缺口冲击强度: 6.7
- 弯曲模量 [MPa]: 10.5
- 硬度: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Water Absorption | 0.060 % @Temperature 23.0 °C | 0.060 % @Temperature 73.4 °F | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 2.00 mm | 0.0025 in/in @Thickness 0.0787 in | 2x60x60mm; ASTM D955 |
| 0.0032 cm/cm @Thickness 3.20 mm | 0.0032 in/in @Thickness 0.126 in | 3.2x7.6x12.6mm; ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0053 cm/cm @Thickness 2.00 mm | 0.0053 in/in @Thickness 0.0787 in | 2x60x60mm; ASTM D955 |
| 0.0079 cm/cm @Thickness 3.20 mm | 0.0079 in/in @Thickness 0.126 in | 3.2x7.6x12.6mm; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength at Break | 111 MPa | 16100 psi | 5 mm/min; ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | 2 mm/min; ISO 178 |
| Compressive Strength | 151 MPa | 21900 psi | 1.3 mm/min; ASTM D695 |
| Shear Strength | 59.0 MPa | 8560 psi | ASTM D732 |
| Izod Impact, Notched (ISO) | 6.70 kJ/m² | 3.19 ft-lb/in² | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.09e+15 ohm-cm | 1.09e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1000 Hz | 3.8 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 16.2 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 411 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 500 V/s in oil; ASTM D149 |
| 21.9 kV/mm @Thickness 1.60 mm, Temperature 23.0 °C | 556 kV/in @Thickness 0.0630 in, Temperature 73.4 °F | 500 V/s in oil; ASTM D149 | |
| Dissipation Factor | 0.011 @Frequency 1000 Hz | 0.011 @Frequency 1000 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 9.44 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 48.3 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-3 |
| Melting Point | 249 °C | 480 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| Flammability Test | 47 | 47 | mm/min, 1.0 mm thickness; ISO 3795 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 295 °C | 518 - 563 °F | |
| Nozzle Temperature | 275 - 300 °C | 527 - 572 °F | |
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 75.0 - 120 °C | 167 - 248 °F | |