- 缺口冲击强度: 0.735
- 断裂伸长率 [%]: 181
- 弯曲模量 [MPa]: 7.85
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm | 0.0040 - 0.010 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 118 MPa @Thickness 3.20 mm | 17100 psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm | 3.0 % @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Flexural Yield Strength | 181 MPa @Thickness 3.20 mm | 26300 psi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Flexural Modulus | 7.85 GPa @Thickness 3.20 mm | 1140 ksi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.735 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.38 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm | 419 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 6.40 mm | 401 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| UL RTI, Electrical | 75.0 °C @Thickness >=1.50 mm | 167 °F @Thickness >=0.0591 in | |
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness >=1.50 mm | 167 °F @Thickness >=0.0591 in | |
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness >=1.50 mm | 167 °F @Thickness >=0.0591 in | |
| Flammability, UL94 | HB @Thickness >=1.50 mm | HB @Thickness >=0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Nozzle Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Melt Temperature | 225 °C | 437 °F | @ Break; ASTM D3418 |
| 255 - 265 °C | 491 - 509 °F | Injection Molding | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |