| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 | ||
| Filler Content | 13 - 17 % | 13 - 17 % | ASTM D2584 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 | ||
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 | ||
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 | ||
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.641 J/cm @Temperature 22.8 °C | 1.20 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 260 - 282 °C | 500 - 540 °F | |||
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |||
| Front Barrel Temperature | 266 - 288 °C | 510 - 550 °F | |||
| Nozzle Temperature | 271 - 299 °C | 520 - 570 °F | reverse tapered recommended | ||
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |||
| Mold Temperature | 82.2 - 104 °C | 180 - 220 °F | thick wall - thin wall | ||
| Drying Temperature | 116 - 135 °C | 240 - 275 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Dew Point | <= -17.8 °C | <= 0.000 °F | |||
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed | ||
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |||
| Back Pressure | 0.345 - 1.21 MPa | 50.0 - 175 psi | keep minimum | ||
| Cushion | 0.635 cm | 0.250 in | |||
| Screw Speed | 20 - 50 rpm | 20 - 50 rpm | |||
| Descriptive Properties | |||||
| Dryer | Dehumidified hopper | ||||
| Fill Rate | Moderate-Fast | ||||
| Hold Pressure | 40-60% of injection pressure | ||||
| Packing Pressure | 50-75% of injection pressure | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.