Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film 物性表: Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film物性表及特性介绍,Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film注塑参数详情,如需Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.4
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 1.40 g/cc
@Temperature 23.0 °C
0.0506 lb/in³
@Temperature 73.4 °F
ASTM D1505-68, method C
Linear Mold Shrinkage 0.013 cm/cm
@Temperature 150 °C,
Time 900 sec
0.013 in/in
@Temperature 302 °F,
Time 0.250 hour
DIN 40634
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
@Temperature 150 °C,
Time 900 sec
0.0030 in/in
@Temperature 302 °F,
Time 0.250 hour
DIN 40634
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 260 MPa37700 psiTest speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Tensile Strength at Yield, TD 265 MPa38400 psiTest speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, MD >= 130 %>= 130 %Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, TD 100 %100 %Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Modulus of Elasticity  4.40 GPa
@Temperature 23.0 °C
638 ksi
@Temperature 73.4 °F
MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
 5.00 GPa
@Temperature 23.0 °C
725 ksi
@Temperature 73.4 °F
TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Coefficient of Friction, Static 0.400.40DIN 53375 or ASTM D1894
 
Optical PropertiesMetricEnglishComments
Haze 8.0 %8.0 %Enlarged measurement angle; ASTM D1003-61, method A
Transmission, Visible 90.0 %90.0 %transparent; thickness not quantified
 
Descriptive Properties
F5-value (MPa)105ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23ºC, 50% r.h.
 110ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23ºC, 50% r.h.

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39285.html

免责声明: 本文 Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4