Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film 物性表: Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film物性表及特性介绍,Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film注塑参数详情,如需Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.4
  • 吸水率 [%]: 0.5
 
Physical PropertiesMetricEnglishComments
Density 1.40 g/cc
@Temperature 23.0 °C
0.0506 lb/in³
@Temperature 73.4 °F
ASTM D1505-68, method C
Water Absorption 0.50 %
@Temperature 23.0 °C
0.50 %
@Temperature 73.4 °F
4 days in water; ASTM D570
Linear Mold Shrinkage 0.010 cm/cm
@Temperature 150 °C,
Time 900 sec
0.010 in/in
@Temperature 302 °F,
Time 0.250 hour
DIN 40634
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
@Temperature 150 °C,
Time 900 sec
0.0030 in/in
@Temperature 302 °F,
Time 0.250 hour
DIN 40634
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, MD 150 MPa21800 psiTest speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Tensile Strength at Yield, TD 200 MPa29000 psiTest speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, MD >= 200 %>= 200 %Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, TD 140 %140 %Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Modulus of Elasticity  3.60 GPa
@Temperature 23.0 °C
522 ksi
@Temperature 73.4 °F
MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
 4.30 GPa
@Temperature 23.0 °C
624 ksi
@Temperature 73.4 °F
TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Coefficient of Friction, Static 0.400.40DIN 53375 or ASTM D1894
 
Electrical PropertiesMetricEnglishComments
Dielectric Constant  2.9
@Frequency 2.40e+8 Hz,
Temperature 23.0 °C
2.9
@Frequency 2.40e+8 Hz,
Temperature 73.4 °F
DIN 40634 or VDE 0345 in air
 2.9
@Frequency 9.30e+9 Hz,
Temperature 23.0 °C
2.9
@Frequency 9.30e+9 Hz,
Temperature 73.4 °F
DIN 40634 or VDE 0345 in air
 3.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
3.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
DIN 40634 or VDE 0345 in air
 3.3
@Frequency 50.0 Hz,
Temperature 23.0 °C
3.3
@Frequency 50.0 Hz,
Temperature 73.4 °F
DIN 40634 or VDE 0345 in air
 3.3
@Frequency 1000 Hz,
Temperature 23.0 °C
3.3
@Frequency 1000 Hz,
Temperature 73.4 °F
DIN 40634 or VDE 0345 in air
 3.6
@Frequency 50.0 Hz,
Temperature 150 °C
3.6
@Frequency 50.0 Hz,
Temperature 302 °F
DIN 40634 or VDE 0345 in air
Dielectric Strength 450 kV/mm
@Temperature 23.0 °C
11400 kV/in
@Temperature 73.4 °F
DC; DIN 40634 or VDE 0345 in air
 135 kV/mm
@Frequency 50.0 Hz,
Temperature 150 °C
3430 kV/in
@Frequency 50.0 Hz,
Temperature 302 °F
DIN 40634 or VDE 0345 in air
 150 kV/mm
@Frequency 50.0 Hz,
Temperature 23.0 °C
3810 kV/in
@Frequency 50.0 Hz,
Temperature 73.4 °F
DIN 40634 or VDE 0345 in air
 
Optical PropertiesMetricEnglishComments
Haze 25 %25 %Enlarged measurement angle; ASTM D1003-61, method A
 
Descriptive Properties
Conductivity of Aqueous Extract (µS/cm)2DIN 40634 or VDE 0345; 1 kHz
F5-value (MPa)105ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23ºC, 50% r.h.
 105ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23ºC, 50% r.h.
Frigen Extract (%)0.05DIN 8944; Cold extraction
Trichloroethylene- Extract (%)0.2DIN 8943; Extracted in Soxhalet apparatus for 2h. Boiled down for 15h at 105ºC

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39278.html

免责声明: 本文 Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4