- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.37
- 弯曲模量 [MPa]: 1.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | STN EN ISO 1183-1 |
| Melt Flow | 15 g/10 min @Load 0.325 kg, Temperature 275 °C | 15 g/10 min @Load 0.716 lb, Temperature 527 °F | STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | STN EN ISO 527-2 |
| Elongation at Break | 3.5 % | 3.5 % | STN EN ISO 527-2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | STN EN ISO 527-2 |
| Flexural Strength | 70.0 MPa | 10200 psi | STN EN ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | STN EN ISO 178 |
| Charpy Impact, Notched | 0.100 J/cm² @Temperature 23.0 °C | 0.476 ft-lb/in² @Temperature 73.4 °F | STN EN ISO 179 |
| 0.100 J/cm² @Temperature -20.0 °C | 0.476 ft-lb/in² @Temperature -4.00 °F | STN EN ISO 179 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | STN EN 11357-1 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Drying Temperature | 110 °C @Time 14400 sec | 230 °F @Time 4.00 hour | |
| Moisture Content | 0.10 % | 0.10 % | STN EN ISO 3344 |
| Injection Pressure | 20.0 - 60.0 MPa | 2900 - 8700 psi | |