- 密度 [g/cm3]: 1.66
- 弯曲强度 [MPa]: 130.0
- 弯曲模量 [MPa]: 10.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO 527-1, 2 |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527-1, 2 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 10.1 GPa | 1460 ksi | ISO 178 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 5.00e+16 ohm | 5.00e+16 ohm | IEC 60093 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ISO 75-1, 2 |
| Flammability, UL94 | V-0 | V-0 | |