- 熔体流动速率 [g/10min]: 40.0
- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.31
- 断裂伸长率 [%]: 92.0
- 弯曲模量 [MPa]: 5.10
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.0090 cm/cm @Thickness 3.20 mm | 0.0080 - 0.0090 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 40 g/10 min @Load 2.16 kg, Temperature 265 °C | 40 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 34 g/10 min @Load 2.16 kg, Temperature 265 °C | 34 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.35 GPa | 776 ksi | 1 mm/min; ISO 527 |
| 5.50 GPa | 798 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.10 GPa | 740 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 |
| 0.300 J/cm @Temperature -30.0 °C | 0.562 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| 2.00 kJ/m² @Temperature -30.0 °C | 0.952 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.100 J/cm² | 0.476 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 46.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 25.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 49.9 µm/m-°C @Temperature -40.0 - 40.0 °C | 27.7 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C | 33.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 34.4 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C @Thickness 3.20 mm | 374 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 175 °C | 347 °F | Rate B/50; ASTM D1525 |
| 175 °C | 347 °F | Rate B/50; ISO 306 | |
| 177 °C | 351 °F | Rate B/120; ISO 306 | |