- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.7
- 缺口冲击强度: 0.7
- 拉伸强度 [MPa]: 47.0
- 断裂伸长率 [%]: 67.0
- 弯曲模量 [MPa]: 1.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.270 % | 0.270 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.70 % | 0.70 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 265 °C | 15 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 2.16 kg, Temperature 265 °C | 13 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
| 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 170 % | 170 % | Type I, 50 mm/min; ASTM D638 |
| >= 200 % | >= 200 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| >= 5.0 % | >= 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.44 GPa | 209 ksi | 50 mm/min; ASTM D638 |
| 1.58 GPa | 229 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 77.0 MPa | 11200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.50 GPa | 218 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| 0.550 J/cm @Temperature -30.0 °C | 1.03 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 0.640 J/cm @Temperature 0.000 °C | 1.20 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 60.0 J @Temperature 23.0 °C | 44.3 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 49.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 94.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 52.2 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 72.0 °C @Thickness 3.20 mm | 162 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 90.0 °C | 194 °F | Rate B/50; ASTM D1525 |
| 92.0 °C | 198 °F | Rate B/50; ISO 306 | |
| 93.0 °C | 199 °F | Rate B/120; ISO 306 | |