- 熔体流动速率 [g/10min]: 21.0
- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 0.5
- 缺口冲击强度: 6.6
- 拉伸强度 [MPa]: 49.0
- 断裂伸长率 [%]: 83.0
- 弯曲模量 [MPa]: 1.94
- 热变形温度 [℃]: 102.0
- 透光率 [%]: 88.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
Moisture Absorption | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 265 °C | 21 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
44 g/10 min @Load 1.20 kg, Temperature 300 °C | 44 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 | |
Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 265 °C | 20 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
42 g/10 min @Load 1.20 kg, Temperature 300 °C | 42 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
Elongation at Break | >= 150 % | >= 150 % | 50 mm/min; ISO 527 |
150 % | 150 % | Type I, 50 mm/min; ASTM D638 | |
Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
Tensile Modulus | 1.84 GPa | 267 ksi | 50 mm/min; ASTM D638 |
1.90 GPa | 276 ksi | 1 mm/min; ISO 527 | |
Flexural Strength | 71.0 MPa | 10300 psi | break, 2 mm/min; ISO 178 |
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Flexural Modulus | 1.94 GPa | 281 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
2.00 GPa | 290 ksi | 2 mm/min; ISO 178 | |
Izod Impact, Notched | 6.60 J/cm | 12.4 ft-lb/in | ASTM D256 |
0.560 J/cm @Temperature -30.0 °C | 1.05 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
5.00 kJ/m² @Temperature -10.0 °C | 2.38 ft-lb/in² @Temperature 14.0 °F | 80*10*4; ISO 180/1A | |
7.00 kJ/m² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
Dart Drop, Total Energy | 95.0 J @Temperature 23.0 °C | 70.1 ft-lb @Temperature 73.4 °F | ASTM D3763 |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 47.2 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
115 µm/m-°C @Temperature -40.0 - 40.0 °C | 63.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 47.2 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
105 µm/m-°C @Temperature -40.0 - 40.0 °C | 58.3 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
Deflection Temperature at 0.46 MPa (66 psi) | 102 °C @Thickness 3.20 mm | 216 °F @Thickness 0.126 in | unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
88.0 °C @Thickness 3.20 mm | 190 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
Vicat Softening Point | 106 °C | 223 °F | Rate B/120; ISO 306 |
107 °C | 225 °F | Rate B/50; ISO 306 | |
108 °C | 226 °F | Rate B/50; ASTM D1525 | |
Flammability, UL94 | V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | UL 94 |
Optical Properties | Metric | English | Comments |
Haze | 2.0 % @Thickness 2.54 mm | 2.0 % @Thickness 0.100 in | ASTM D1003 |
Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |