SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Europe-Africa-Middle East)物性表参数

熔体流动速率 [g/10min]: 4.0
密度 [g/cm3]: 1.2
吸水率 [%]: 0.37
缺口冲击强度: 8.54
拉伸强度 [MPa]: 57.0
断裂伸长率 [%]: 94.0
弯曲模量 [MPa]: 2.00
热变形温度 [℃]: 116.0
透光率 [%]: 88.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D792
Density	1.20 g/cc	0.0434 lb/in³	ISO 1183
Moisture Absorption	0.130 %	0.130 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.37 %	0.37 %	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	4.0 g/10 min @Load 2.16 kg, Temperature 265 °C	4.0 g/10 min @Load 4.76 lb, Temperature 509 °F	ASTM D1238
Melt Index of Compound	3.0 g/10 min @Load 2.16 kg, Temperature 265 °C	3.0 g/10 min @Load 4.76 lb, Temperature 509 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D638
	60.0 MPa	8700 psi	50 mm/min; ISO 527
Tensile Strength, Yield	57.0 MPa	8270 psi	Type I, 50 mm/min; ASTM D638
	60.0 MPa	8700 psi	50 mm/min; ISO 527
Elongation at Break	92 %	92 %	Type I, 50 mm/min; ASTM D638
	117 %	117 %	50 mm/min; ISO 527
Elongation at Yield	5.8 %	5.8 %	50 mm/min; ISO 527
	6.0 %	6.0 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.18 GPa	316 ksi	1 mm/min; ISO 527
	2.37 GPa	344 ksi	50 mm/min; ASTM D638
Flexural Strength	89.0 MPa	12900 psi	break, 2 mm/min; ISO 178
Flexural Yield Strength	94.0 MPa	13600 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
	2.22 GPa	322 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	8.54 J/cm	16.0 ft-lb/in	ASTM D256
	2.00 J/cm @Temperature -30.0 °C	3.75 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	10.0 kJ/m²	4.76 ft-lb/in²	80104; ISO 180/1A
	8.00 kJ/m² @Temperature -10.0 °C	3.81 ft-lb/in² @Temperature 14.0 °F	80104; ISO 180/1A
	8.00 kJ/m² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	70.0 J @Temperature 23.0 °C	51.6 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	60.0 µm/m-°C @Temperature 23.0 - 60.0 °C	33.3 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
	104 µm/m-°C @Temperature -40.0 - 40.0 °C	57.8 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	104 µm/m-°C @Temperature -40.0 - 40.0 °C	57.8 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	70.0 µm/m-°C @Temperature 23.0 - 60.0 °C	38.9 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
	104 µm/m-°C @Temperature -40.0 - 40.0 °C	57.8 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	104 µm/m-°C @Temperature -40.0 - 40.0 °C	57.8 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Thermal Conductivity	0.230 W/m-K	1.60 BTU-in/hr-ft²-°F	ISO 8302
Deflection Temperature at 0.46 MPa (66 psi)	116 °C @Thickness 3.20 mm	241 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	102 °C	216 °F	Edgew 120104 sp=100mm; ISO 75/Ae
	104 °C @Thickness 3.20 mm	219 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	121 °C	250 °F	Rate B/50; ISO 306
	123 °C	253 °F	Rate B/120; ISO 306
	123 °C	253 °F	Rate B/50; ASTM D1525

Optical Properties	Metric	English	Comments
Refractive Index	1.576	1.576	ASTM D542
Haze	1.5 % @Thickness 2.54 mm	1.5 % @Thickness 0.100 in	ASTM D1003
Transmission, Visible	88 %	88 %	2.54 mm; ASTM D1003

关键词:
PET
供应
SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Europe-Africa-Middle East)