SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Europe-Africa-Middle East)物性表参数

熔体流动速率 [g/10min]: 10.0
密度 [g/cm3]: 1.16
吸水率 [%]: 0.37
缺口冲击强度: 8.0
拉伸强度 [MPa]: 43.0
断裂伸长率 [%]: 65.0
弯曲模量 [MPa]: 1.60
热变形温度 [℃]: 79.0
透光率 [%]: 85.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D792
Density	1.16 g/cc	0.0419 lb/in³	ISO 1183
Moisture Absorption	0.150 %	0.150 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.37 %	0.37 %	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0040 - 0.0060 cm/cm @Thickness 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	10 g/10 min @Load 2.16 kg, Temperature 265 °C	10 g/10 min @Load 4.76 lb, Temperature 509 °F	ASTM D1238
	14 g/10 min @Load 1.20 kg, Temperature 300 °C	14 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Melt Index of Compound	10 g/10 min @Load 2.16 kg, Temperature 265 °C	10 g/10 min @Load 4.76 lb, Temperature 509 °F	MVR [cm^3/10 min]; ISO 1133
	13 g/10 min @Load 1.20 kg, Temperature 300 °C	13 g/10 min @Load 2.65 lb, Temperature 572 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	50 mm/min; ISO 527
	46.0 MPa	6670 psi	Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield	43.0 MPa	6240 psi	Type I, 50 mm/min; ASTM D638
	45.0 MPa	6530 psi	50 mm/min; ISO 527
Elongation at Break	150 %	150 %	Type I, 50 mm/min; ASTM D638
	>= 150 %	>= 150 %	50 mm/min; ISO 527
Elongation at Yield	4.6 %	4.6 %	50 mm/min; ISO 527
	5.0 %	5.0 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	1.48 GPa	215 ksi	50 mm/min; ASTM D638
	1.50 GPa	218 ksi	1 mm/min; ISO 527
Flexural Strength	58.0 MPa	8410 psi	break, 2 mm/min; ISO 178
Flexural Yield Strength	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	1.60 GPa	232 ksi	1.3 mm/min, 50 mm span; ASTM D790
	1.60 GPa	232 ksi	2 mm/min; ISO 178
Izod Impact, Notched	8.00 J/cm	15.0 ft-lb/in	ASTM D256
	2.00 J/cm @Temperature -30.0 °C	3.75 ft-lb/in @Temperature -22.0 °F	ASTM D256
	6.40 J/cm @Temperature -20.0 °C	12.0 ft-lb/in @Temperature -4.00 °F	ASTM D256
Izod Impact, Notched (ISO)	45.0 kJ/m²	21.4 ft-lb/in²	80104; ISO 180/1A
	11.0 kJ/m² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	30.0 kJ/m² @Temperature -10.0 °C	14.3 ft-lb/in² @Temperature 14.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	7.10 J/cm²	33.8 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	81.0 J @Temperature 23.0 °C	59.7 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	83.0 µm/m-°C @Temperature -40.0 - 40.0 °C	46.1 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
	110 µm/m-°C @Temperature -40.0 - 40.0 °C	61.1 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
CTE, linear, Transverse to Flow	89.0 µm/m-°C @Temperature -40.0 - 40.0 °C	49.4 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
	110 µm/m-°C @Temperature -40.0 - 40.0 °C	61.1 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	79.0 °C @Thickness 3.20 mm	174 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	81.0 °C	178 °F	Flatw 80104 sp=64mm; ISO 75/Af
	82.0 °C	180 °F	Edgew 120104 sp=100mm; ISO 75/Ae
	75.0 °C @Thickness 3.20 mm	167 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	92.0 °C	198 °F	Rate B/50; ISO 306
	97.0 °C	207 °F	Rate B/120; ISO 306
	97.0 °C	207 °F	Rate B/50; ASTM D1525

Optical Properties	Metric	English	Comments
Haze	4.0 % @Thickness 2.54 mm	4.0 % @Thickness 0.100 in	ASTM D1003
Transmission, Visible	85 %	85 %	2.54 mm; ASTM D1003