- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 0.42
- 缺口冲击强度: 0.7
- 拉伸强度 [MPa]: 61.0
- 断裂伸长率 [%]: 98.0
- 弯曲模量 [MPa]: 4.00
- 热变形温度 [℃]: 131.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D 792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.14 % | 0.14 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % @Temperature 23.0 °C | 0.42 % @Temperature 73.4 °F | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 265 °C | 7.0 g/10 min @Load 11.0 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 8.0 g/10 min @Load 5.00 kg, Temperature 266 °C | 8.0 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D 1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, H358/30 | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D 638 |
| 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 | |
| 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | |
| 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D 638 |
| 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 | |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| 67.0 MPa | 9720 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | 50 mm/min; ISO 527 | |
| 30 % | 30 % | Type I, 50 mm/min; ASTM D 638 | |
| 60 % | 60 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.3 % | 3.3 % | Type I, 50 mm/min; ASTM D 638 |
| 3.6 % | 3.6 % | 5 mm/min; ISO 527 | |
| 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D 638 | |
| 3.8 % | 3.8 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
| 4.60 GPa | 667 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 |
| 4.25 GPa | 616 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.700 J/cm @Temperature -30.0 °C | 1.31 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 0.800 J/cm @Temperature 0.000 °C | 1.50 ft-lb/in @Temperature 32.0 °F | ASTM D 256 | |
| 0.900 J/cm @Temperature 23.0 °C | 1.69 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 10.0 kJ/m² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 90.0 J | 66.4 ft-lb | Multiaxial Impact; ISO 6603 |
| 60.0 J @Temperature 23.0 °C | 44.3 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 | |
| 60.0 J @Temperature -20.0 °C | 44.3 ft-lb @Temperature -4.00 °F | Instrumented Impact Total Energy; ASTM D 3763 | |
| Taber Abrasion, mg/1000 Cycles | 30 @Load 1.00 kg | 30 @Load 2.20 lb | CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 23.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 48.0 µm/m-°C @Temperature -30.0 - 80.0 °C | 26.7 µin/in-°F @Temperature -22.0 - 176 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 35.6 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 68.0 µm/m-°C @Temperature -30.0 - 80.0 °C | 37.8 µin/in-°F @Temperature -22.0 - 176 °F | ISO 11359-2 | |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 132 °C @Thickness 3.20 mm | 270 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 113 °C @Thickness 3.20 mm | 235 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ASTM D 1525 |
| 137 °C | 279 °F | Rate B/50; ISO 306 | |
| 139 °C | 282 °F | Rate B/120; ISO 306 | |