- 熔体流动速率 [g/10min]: 16.0
- 缺口冲击强度: 2.94
- 拉伸强度 [MPa]: 41.2
- 弯曲模量 [MPa]: 1.91
- 硬度: 106.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 250 °C | 16 g/10 min @Load 22.0 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 41.2 MPa | 5970 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 60.8 MPa | 8820 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm @Thickness 3.17 mm | 5.51 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm | 194 °F @Thickness 0.252 in | ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |