- 吸水率 [%]: 0.09
- 缺口冲击强度: 0.294
- 断裂伸长率 [%]: 83.4
- 弯曲模量 [MPa]: 2.45
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Water Absorption | 0.090 % | 0.090 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.020 cm/cm | 0.0080 - 0.020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.020 cm/cm | 0.0080 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Yield Strength | 83.4 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 0.551 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 | 3.0 | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |