- 熔体流动速率 [g/10min]: 28.0
- 吸水率 [%]: 0.1
- 拉伸强度 [MPa]: 191.0
- 断裂伸长率 [%]: 279
- 弯曲模量 [MPa]: 9.32
- 硬度: 119.0
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 3.00 mm | 0.0020 - 0.0040 in/in @Thickness 0.118 in | ASTM D955 |
| Melt Flow | 28 g/10 min @Load 5.00 kg, Temperature 265 °C | 28 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 191 MPa | 27700 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 279 MPa | 40500 psi | ASTM D790 |
| Flexural Modulus | 9.32 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Unnotched | 0.932 J/cm @Thickness 3.17 mm | 1.74 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | ASTM D150 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
| Dissipation Factor | 0.016 @Frequency 1.00e+6 Hz | 0.016 @Frequency 1.00e+6 Hz | ASTM D150 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm | HB @Thickness 0.0625 in | |