- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.932
- 断裂伸长率 [%]: 216
- 弯曲模量 [MPa]: 9.81
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 137 MPa | 19900 psi | ASTM D638 |
| Elongation at Break | 3.6 % | 3.6 % | ASTM D638 |
| Flexural Yield Strength | 216 MPa | 31300 psi | ASTM D790 |
| Flexural Modulus | 9.81 GPa | 1420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.932 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 1.74 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 | 4.0 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |