- 熔体流动速率 [g/10min]: 35.0
- 缺口冲击强度: 5.87
- 拉伸强度 [MPa]: 57.2
- 断裂伸长率 [%]: 86.2
- 弯曲模量 [MPa]: 2.34
- 热变形温度 [℃]: 127.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 5.00 kg, Temperature 260 °C | 35 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | ASTM D638 |
| Tensile Modulus | 2.17 GPa | 315 ksi | ASTM D638 |
| Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm | 11.0 ft-lb/in | 73°F, 0.125 in.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 260 °F | unannealed, .250in; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 245 °F | unannealed, .125in; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 243 - 271 °C | 470 - 520 °F | |
| Middle Barrel Temperature | 249 - 277 °C | 480 - 530 °F | |
| Front Barrel Temperature | 257 - 282 °C | 495 - 540 °F | |
| Nozzle Temperature | 254 - 274 °C | 490 - 525 °F | |
| Melt Temperature | 260 - 279 °C | 500 - 535 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Screw Speed | 40 - 75 rpm | 40 - 75 rpm | |