- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.05
- 缺口冲击强度: 1.6
- 断裂伸长率 [%]: 206
- 弯曲强度 [MPa]: 137.0
- 弯曲模量 [MPa]: 9.80
- 热变形温度 [℃]: 225.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength, Ultimate | 137 MPa | 19900 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 9.80 GPa | 1420 ksi | ASTM D790 |
| Compressive Yield Strength | 103 MPa | 14900 psi | ASTM D695 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 33 | 33 | ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm | 635 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | 215 V | 215 V | IEC test |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |